Evaluation of rheological properties of artisan and technified sesame pasta
Evaluación de las propiedades reológicas de pastas de ajonjolí artesanal y tecnificada
Autor
Acevedo, Diofanor
Marrugo, Yesid
Montero, Piedad
Resumen
Sesame pastes are a colloidal suspension composed mainly of hydrophilic solids suspended in oil. In this work two types of sesame paste, one obtained by the traditional process and the other one through a technified process were produced; proximate analyzes were performed and the effects of manufacturing processes on the rheological behavior and stability was determined. The viscosity profile obtained for both samples indicated a typical behavior of pseudoplastic. The syneresis observed for the paste elaborated in the traditional maner was higher, being 40%, whereas that for tech paste was 15%, reason for the higher stability of the latter one. It is concluded that the technified process is more efficient and recommended for the development of this product type. Las pastas de ajonjolí son una suspensión coloidal compuesta, principalmente, de sólidos hidrófilos suspendidos en aceite. En este trabajo, se elaboraron dos tipos de pastas de ajonjolí: una por el método artesanal y la otra mediante una técnica tecnificada; posteriormente, se le realizaron análisis proximales y se determinaron los efectos de los procesos de elaboración en el comportamiento reológico y la estabilidad. El perfil de viscosidad obtenido para las pastas indicó un comportamiento pseudoplástixco. La sinéresis de la pasta elaborada artesanalmente fue mayor, siendo de 40%, mientras que para la pasta tecnificada fue de 15%, razón por la cual, fue más estable. Por lo que se concluye, que el proceso tecnificado es más eficiente y recomendable para la elaboración de este tipo de productos.