Evaluation of the physical and biological properties of Ti-34Nb-6Sn/Mg alloy obtained by powder metallurgy for use as biomaterial
Registro en:
1516-1439
25
10.1590/1980-5373-MR-2021-0233
0000-0001-7707-7821
19.4
40.5
Autor
ROSSI, MARIANA C.
STIEVANI, FERNANDA de C.
PFEIFER, JOAO P.H.
MARTINEZ, LUIS G.
BORRAS, VICENTE A.
SAEKI, MARGARIDA J.
ALVES, ANA L.G.
Resumen
Ti-34Nb-6Sn alloy were prepare by powder metallurgy milled in two different times (40 and 60 min) using Ti and Nb hydrides with or without Mg, as spacer then sintered at 700??C and 800??C. Characterizations were made by scanning electron microscope (SEM), X-ray diffractometer (XRD) and by Archimedes. Microhardness was measured by Vickers microhardness. Mesenchymal stem cells derived from equine bone marrow (BMMSCs) were used to evaluate the sample cytotoxicity. Hydration and dehydration process was confirmed, also the formation of brittle particles during the milling. Materials were structured under ?? and ?? phase, and the samples that received Mg as a spacer had slightly lower ?? phase content compared to samples without Mg, suggesting difficult ??????? transformation due to the presence of barriers formed by pores. Mg provided greater porosity, and prepared milled in a shorter time promoted an increase in the macropores. Microhardness was similar to that of commercial materials (i.e., CP-Ti and also to other alloys with similar nominal composition. Cells treated with conditioned medium with the samples showed viability comparable to the control group, and after 48 h of culture on the samples, there was significant growth and more circular morphology, when adhered on materials that received Mg. Funda????o de Amparo ?? Pesquisa do Estado de S??o Paulo (FAPESP) FAPESP: 17/13876-2; 19/24237-6
Ítems relacionados
Mostrando ítems relacionados por Título, autor o materia.
-
Effect of added porosity on a novel porous Ti-Nb-Ta-Fe-Mn alloy exposed to simulated body fluid
Guerra C.; Sancy M.; Walczak M.; Martínez C.; Ringuedé A.; Cassir M.; Han J.; Ogle K.; de Melo H.G.; Salinas V.; Aguilar C. (Elsevier Ltd, 2020) -
Influ??ncia do estanho na absor????o de hidrog??nio em ligas ?? base de LaMgAlMnCoNiSn
FIM, RAFAEL G.T.; TAKIISHI, HIDETOSHI; PROGRAMA INSTITUCIONAL DE BOLSAS DE INICIA????O CIENT??FICA, 20.; PROGRAMA DE BOLSAS E INICIA????O CIENT??FICA CNEN, 11.; PROGRAMA INSTITUCIONAL DE BOLSAS DE INICIA????O DESENVOLVIMENTO TECNOL??GICO E INOVA????O, 4. -
Influence of thermal and mechanical cycling on the flexural strength of ceramics with titanium or gold alloy frameworks
Oyafuso, Denise Kanashiro; Özcan, Mutlu; Bottino, Marco Antonio; Itinoche, Marcos Koiti