Análise de corpos de prova mandibulares utilizados para avaliação de sistema de fixação óssea = Analysis of mandibular test specimens used to assess a bone fixation system
Analysis of mandibular test specimens used to assess a bone fixation system
Registro en:
Autor
Baccarin, Leandro Stocco, 1978-
Institución
Resumen
Orientador: Luis Augusto Passeri Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Ciências Médicas Resumo: Objetivo: O objetivo deste trabalho é avaliar, por meio de testes biomecânicos, se materiais sintéticos diferentes, empregados para a confecção de corpos de prova apresentam comportamento biomecânico diferente, em comparação aos demais, ao simular in vitro a resistência ao carregamento de um método de fixação consagrado para OSRM. Material: 30 réplicas de hemimandíbulas humana, sintéticas e padronizadas, com OSRM, divididas em três grupos de 10 amostras cada: Grupo A - plástico ABS, Grupo B - Poliamida, e Grupo C - Poliuretano. Estas foram fixadas por três parafusos bicorticais posicionais (16 mm de comprimento, sistema 2.0 mm), em disposição "L" invertido, utilizando-se guias de perfuração e avanço de 5 mm. Métodos: Cada amostra foi submetida ao carregamento linear vertical e os valores de resistência ao carregamento registrado em 1, 3, 5, 7 e 10 mm de deslocamento. As médias e desvio padrão foram comparados, empregando-se análise de variância (p<0.05) e pelo teste Tukey. Resultados: Notou-se uma tendência de menores valores no grupo B em relação aos grupos A e C. Nos deslocamentos 3 e 5 mm, houve uma diferença entre os grupos A e C para o grupo B (p<0.05). Nos deslocamentos 7 e 10 mm houve diferença entre os 3 grupos sendo os maiores valores encontrados no grupo C e os menores no grupo B (p<0.05). Conclusões: Levando-se em consideração os resultados obtidos e o comportamento de cada material utilizado como substrato, podemos considerar que ocorreram diferenças significativas entre os materiais, quando comparados entre si Abstract: Purpose: The aim of this study was to assess through biomechanical testing if different synthetic materials used to fabricate test specimens have a different biomechanical behavior in comparison with other materials when simulating in vitro load resistance of a fixation method established for SSRO. Material: Thirty synthetic and standardized human hemimandible replicas with SSRO were divided into three groups of 10 samples each. Group A - ABS plastic; Group B - Polyamide and Group C - Polyurethane. These were fixated with three bicortical position screws (16 mm in length, 2.0mm system) in an inverted L pattern using perforation guide and 5 mm advancement. Methods: Each sample was submitted to linear vertical load and load strength values were recorded at 1, 3, 5, 7 and 10 mm of displacement. The means and standard deviation were compared using the Analysis of Variance (p<0.05) and the Tukey's test. Results: A tendency for lower values was observed in Group B in comparison with Groups A and C. At 3 and 5 mm of displacement, a difference between Groups A and C was found in comparison with Group B (p<0.05). At 7 and 10 mm of displacement a difference was found among the 3 groups, in which Group C showed the highest values and Group B the lowest (p<0.05). Conclusions: Taking into consideration the results obtained and the behavior of each material used as a substrate, significant differences occurred among the materials when compared among them Mestrado Fisiopatologia Cirúrgica Mestre em Ciências
Ítems relacionados
Mostrando ítems relacionados por Título, autor o materia.
-
Avaliação tridimensional da posição do forame e canal mandibulares e sua relação com a osteotomia sagital dos ramos mandibulares nas diferentes classes esqueléticas
Castro, Raquel Werczler Queiroz de, 1990- -
Evaluación de patrones de expresión génica en respuesta a distintas concentraciones DHA en tejido hepático y mandibular de Seriola lalandi in vitro
Martínez Moncada, Víctor; Gormaz Araya, Juan Guillermo; UNIVERSIDAD DE CHILE (2018)Seriola lalandi es un pez teleósteo marino con un alto potencial para su uso en la acuicultura. Sin embargo, una de las principales limitaciones para su cultivo es la aparición impredecible de deformidades mandibulares en ...