Wood is used for furniture, panel making and civil construction. However, the species used are restricted to a small group that is intensively exploited, which poses a risk to the availability of these species in the forest massifs. Thus, it is necessary to carry out studies in relation to less exploited species, for their inclusion in the market. The objective was to characterize the radial variation of the physical properties of tauari wood. Logs from tauari trees were used, from which 120 specimens were made, subjected to saturation, drying and acclimatization, to obtain data for the calculation of apparent density (?a) and basic (?b), porosity (?), linear (?l, ?t and ?r) and volumetric (?V) shrinkages and the anisotropy coefficient (T/R). The wood was characterized as moderately heavy (?b = 0.68 g cm-3), with a moderate tendency to warping and a low anisotropy coefficient (<1.4), indicating that the material has good dimensional stability and can present itself as an alternative to intensely explored species, as it is found in a large part of the Amazon.La madera se utiliza para muebles, fabricación de paneles y construcción civil. Sin embargo, las especies utilizadas están restringidas a un pequeño grupo que se explota intensamente, lo que representa un riesgo para la disponibilidad de estas especies en bosques masivos. Por ello, es necesario realizar estudios en relación a las especies menos explotadas para su inclusión en el mercado. El objetivo fue caracterizar la variación radial de las propiedades físicas de la madera de tauari. Se utilizaron troncos de árboles de tauari, de los cuales se elaboraron 120 especímenes, sometidos a saturación, secado y aclimatación, para obtener datos para el cálculo de densidad aparente (?a) y básica (?b), porosidad (?), lineal (?l, ?t y ?r) y contracciones volumétricas (?V) y el coeficiente de anisotropía (T/R). La madera se caracterizó por ser moderadamente pesada (?b = 0,68 g cm-3), con moderada tendencia al alabeo y bajo coeficiente de anisotropía (<1,4), indicando que el material tiene buena estabilidad dimensional y puede presentarse como una alternativa a especies intensamente exploradas, ya que se encuentra en gran parte de la Amazonía.A madeira é utilizada para movelaria, confecção de painéis e construção civil. Contudo as espécies utilizadas restringem-se a um pequeno grupo que é intensamente explorado, isto oferece risco à disponibilidade dessas espécies nos maciços florestais. Dessa forma é necessária a realização de estudos em relação a espécies menos exploradas para a inclusão das mesmas no mercado. Objetivou-se caracterizar a variação radial das propriedades física da madeira de tauari. Foram utilizadas toras de árvores de tauari, a partir das quais confeccionou-se 120 corpos de prova, submetidos à saturação, secagem e aclimatação, para obtenção de dados para os cálculos de densidade aparente (?a) e básica (?b), porosidade (?), contrações lineares (?l, ?t e ?r) e volumétrica (?V) e o coeficiente de anisotropia (T/R). A madeira foi caracterizada como moderadamente pesada (?b = 0,68 g cm-3), com tendência moderada à empenamentos e baixo coeficiente de anisotropia (<1,4), indicando que o material tem boa estabilidade dimensional e pode apresentar-se como alternativa às espécies intensamente exploradas, pois é encontrada em grande parte da Amazônia.