Effects of gamma radiation absorbed dose on VBC grafting onto LDPE films and on anion exchange membrane fuel cells performance
Registro en:
0000-0002-5972-5933
0000-0002-0127-8130
Autor
KODAMA, YASKO
BIANCOLLI, ANA L.
BARBOSA, ANDREY
SANTIAGO, ELISABETE
INTERNATIONAL CONFERENCE ON APPLICATIONS OF RADIATION SCIENCE AND TECHNOLOGY, 2nd
Resumen
Anion-Exchange Membranes (AEMs) are polymer electrolytes that conduct anions, such as OH- and Cl-, as
they contain positively charged [cationic] groups (typically) bound covalently to a polymer backbone. It is
possible to take advantage of this characteristic for electrochemical devices, such as fuel cells. Fuel cells are
electrochemical systems that convert chemical energy into electrical energy through continuous feeding fuel.
These systems represent an alternative technology of electricity with great efficiency and large applicability
in the areas of portable, stationary, and automotive powers due to important improvements achieved in
the field of electrocatalysis in the past decade. In this present research, AEMs based on films of low density
polyethylene (LDPE), were synthesized by radiation induced grafting with 4-vinylbenzylchloride (VBC)
monomer solution using direct method. Samples were irradiated with gamma rays from Co-60 at room temperature,
in nitrogen and/or air atmosphere at Gammacell of IPEN-CNEN/SP. Several radiation absorbed doses
(10-30kGy) were used to study degree of grafting (DoG) of VBC onto LDPE gamma irradiated films. The
optimization of parameters and conditions of irradiation have been evaluated by degree of grafting. Functionalization
with quaternary ammonium groups was made in water by using trimethylamine (TMA). After,
treatment with NaCl for Cl-groups addition was performed, responsible for ionic exchange and ionic groups
stabilization. Then, hydroxylation reaction was performed with KOH for hydroxyl groups addition (anionic
exchange of Cl- groups by OH-). Besides DoG, characterization of the ion exchange membranes was performed
at IPEN-CNEN/SP involving determination of physico-chemical properties such as water uptake, ion
exchange capacity and ionic conductivity. Furthermore, AC impedance spectroscopy, scanning electron microscopy
(SEM) were performed for characterization of radiation grafted membranes. DoG increased with
radiation absorbed dose increase, homopolymerization affected some grafted membranes at high radiation
absorbed doses. Also, atmosphere of irradiation affected the DoG. The resulting AEM synthesized by RIG
of VBC onto LDPE with 30 kGy radiation absorbed was tested in a fuel cell and reached a maximum power
density of 942 mW cm???2 at 80 ??? with gases flow of 0.8 L min-1 and 0.5 L min-1 for H2 and O2, respectively.