The electrical response of Ba(Ti0.90Zr0.10)O3 (BZT) ceramics obtained by the mixed oxide method as a functionof tungsten content was investigated. According to X-ray diffraction analysis the single phase BZT1W (1wt.% W doped BZT) and BZT2W (2 wt.% W doped BZT) ceramics, crystallized in a perovskite structure, wereobtained. It is also shown that tungsten substituted ceramics can be sintered at a reduced temperature whencompared to the undoped BZT. Electron paramagnetic resonance (EPR) analyses reveals that substitution ofTi4+ by W6+ causes distortion in the crystal structure changing lattice parameter. Substitution of W6+ on B-siteof ABO3 perovskite BZT ceramics shifted the phase transition to lower temperatures up to a tungsten contentof 2 wt.% leading to a relaxor-like behaviour.Keywords: donor dopant; ceramics; dielectric response; mixed oxide methodUniversidade Federal de Itajubá- Unifei - Campus Itabira, Rua São Paulo 377, Bairro Amazonas, 355, 35900-37, Itabira, Minas Gerais, BrazilUniversidade Estadual Paulista Júlio de Mesquita Filho, Faculdade de Ciências e Letras de Assis, Assis, Avenida Dom Antonio, 2100, Vila Universitária, CEP 19806-900, SP, BrasilUniversidade Estadual Paulista- Unesp - Faculdade de Engenharia de Campus Itabira, Av. Dr Ariberto Pereira da Cunha 333, Bairro Pedregulho, P.O. Box 355, 12.516-410, Guaratinguetá, São Paulo, BrazilLaboratório Interdisciplinar em Cerâmica, Instituto de Química, Universidade Estadual Paulista, P.O. Box 355, 14801-907 Araraquara, São Paulo, Brazil