Fabrication and study of thin transparent conductive films prepared by Spin Coating from metal nano-wires
Fecha
2016-07-08Autor
Bernal, Andrés M.
Ardila, Angel M.
Vega Verdugo, Marisol
Institución
Resumen
(Eng) Transparent conductive thin films on glass substrates from metal nano-wires were produced by the
spin coating method by varying the speed of rotation between 1000 and 9000 RPM. Morphological
and structural properties of the deposited layers were studied by Scanning Electron Microscopy (SEM).
The electrical and optical properties were studied as a function of layer thickness by the Van Der Paw
method and transmittance measurements in the range between 350 and 800 nm. A correlation between the
thickness of the deposited layers and their electrical and optical properties is obtained, showing less sheet
resistance to larger thickness while its transmittance decreases. Samples with sheet resistance of about 20
Ω/sq and with average 77% light transmittance at 550 nm were obtained. (Spa) Se fabricaron películas delgadas conductoras y transparentes sobre sustratos de vidrio a partir de nano-hilos
metálicos por el método spin coating, variando la velocidad de rotación entre 1000 y 9000 revoluciones
por minuto. De las capas depositadas se hizo un estudio de sus propiedades morfológicas y estructurales
mediante microscopía electrónica de barrido (SEM). Las propiedades eléctricas y ópticas se estudiaron
en función del espesor de las capas mediante el método de Van Der Paw y con medidas de transmitancia
en el rango entre 350 y 800 nm. Se encuentra una correlación entre el espesor de las capas depositadas y
sus propiedades eléctricas y ópticas, presentando menor resistencia de hoja a mayores espesores a la vez
que su transmitancia disminuye. Se obtuvieron muestras con resistencia de hoja alrededor de 20 Ω/sq y
transmitancia óptica promedio de 77% a 550 nm.