The resins are affected by many factors such as the presence of an inhibited layer of oxygen which contributes to the last layer of resin to have a partial polymerization which brings problems such as surface pigmentations. Objective: Determine the surface pigmentation in monohybrid resins which are subjected to the glycerin application versus conventional. Methods: 40 disc samples with 10 mm diameter and 2 mm thickness were made, which were distributed in 4 groups of 10 samples each one. The first group: Composite Brilliant NG resin discs (Coltene) with glycerin application. Second Group: Composite Opallis resin discs (FGM) with glycerin application. Third group: resin discs will be Composite Brilliant NG (Coltene) with the conventional polishing application. Finally, the group four: resin discs of Composite Opallis (FGM) with the conventional polishing application. The samples were exposed for 3 hours a day for 15 days in a pigmenting agent (black soda). The color of the samples was taken before and after being submerged in the pigmenting agent through Vita Easy-shade V and we used the Shapiro-Wilk, Wilcoxon, Kruskal Wallis test for the statistical analysis. Results: The samples with conventional polishing were pigmented in a larger scale (5 to 10) while the ones which were applied glycerin were pigmented in a smaller scale (1 to 3) Conclusion: The glycerin application helps to reduce the pigmentation of the resins. Key words: Glycerin, oxygen, polymerization.Las resinas se ven afectadas por muchos factores como la presencia de una capa inhibida de oxígeno, contribuyendo a que la última capa de resina tenga una polimerización parcial, trayendo consigo problemas posteriores como pigmentaciones superficiales. Objetivo: Determinar la pigmentación superficial en resinas nanohíbridas sometidas a la aplicación glicerina vs el pulido convencional. Métodos: Se confeccionaron 40 muestras en forma de disco con 10 mm de diámetro y 2 mm de espesor distribuidos en 4 grupos de 10 muestras cada uno: Grupo 1, discos de resina Composite Brilliant NG (Coltene) con aplicación de glicerina; Grupo 2, discos de resina de Composite Opallis (FGM) con aplicación de glicerina; Grupo 3, discos de resina serán de Composite Brilliant NG (Coltene) con la aplicación del pulido convencional; Grupo 4, discos de resina de Composite Opallis (FGM) con la aplicación del pulido convencional. Las muestras se expusieron durante 3 horas al día por 15 días en un agente pigmentante (soda negra), se tomó el color de las muestras antes y después de ser sumergidas en el agente pigmentante por medio del Vita Easyshade V, para el análisis estadístico se utilizó la prueba de Shapiro-Wilk, Wilcoxon, Kruskal Wallis. Resultados: Las muestras con pulido convencional se pigmentaron en una mayor escala (5 a 10), mientras que las que se aplicaron glicerina se pigmentaron en una menor escala (1 a 3) Conclusión: La aplicación de glicerina ayuda a disminuir la pigmentación de las resinas. Palabras Claves: Glicerina, oxígeno, polimerización