Oxidación catalítica del ion ferroso en medio ácido mediante aire y carbón activado dopado con metales de transición
Registro en:
Tesis (Ingeniera Química), Universidad San Francisco de Quito, Colegio de Ciencias e Ingenierías; Quito, Ecuador, 2020
Autor
Torre Miranda, Ernesto David de la
Institución
Resumen
In this study, the catalytic oxidation of Fe2+ to Fe3+ is carried out with active aeration using
activated carbon doped with Au, Pt and Ru, as an alternative to traditional oxidative methods
for its application in the ferric acid leaching of copper sulfides. An impregnation of Au, Pt, Ru
in both granular (2 mm) and powdered (38 μm) activated carbons (274 m2
/g) was performed.
Using standard solutions (48 mg/L) of these metals in contact with 4 g/L of activated carbon,
for 2 hours in a stirred bed. Then, 5,6 g/L of NaBH4 was added for 3 hours to reduce the metal.
The solution was filtrated and analyzed valued by UV-Vis analysis, while the obtained solid
was dried... En este estudio, la oxidación catalítica de Fe2+ a Fe3+ se lleva a cabo con aireación activa
utilizando carbón activado dopado con Au, Pt y Ru, como una alternativa a los métodos
oxidativos tradicionales para su aplicación en la lixiviación ácido férrica de sulfuros de cobre.
Se realizó una impregnación de Au, Pt, Ru tanto en carbones activados granulares (2 mm)
como en polvo (38 μm) (274 m2
/g). Usando soluciones estándar (48 mg/L) de estos metales en
contacto con 4 g/L de carbón activado, durante 2 horas en un lecho agitado, se añadieron
5,6 g/L de NaBH4 durante 3 horas para reducir el metal...