Comparative Study of the Bioactivity of Two Bioceramic Materials
Registro en:
10.15517/ijds.v21i2.37061
Autor
Trujillo-Hernández, Margarita
Flores-Ventura, Rebeca E.
Suárez-Porras MSc, Angélica
García-González PhD, Leandro
Hernández-Torres PhD, Julián
Zamora-Peredo PhD, Luis
Suárez-Franco DDS, MSc, PhD, José Luis
Institución
Resumen
Calcium silicate-based materials have been shown to be bioactive due to their ability to produce biologically compatible carbonated apatite. The objective of this study was to analyze the bioactivity of Biodentine ™ and MTA Repair HP® in contact with human dentine discs, which were sealed and divided randomly to form four groups: group 1 Biodentine™, group 2 MTA Repair HP®, positive control group MTA Angelus® and negative control group IRM®, which were incubated in PBS solution for 10 days, for a subsequent analysis by means of MEB-EDS and Raman spectroscopy. The three calcium-based materials analyzed in this study proved to be bioactive because upon contact with a phosphate-based solution they were triggered at the onset of amorphous calcium phosphate, as the precursor during the formation of carbonated apatite. Los materiales a base de silicato de calcio han demostrado ser bioactivos debido a su capacidad para producir apatita carbonatada biológicamente compatible. El objetivo de este estudio fue analizar la bioactividad de Biodentine™ y MTA Repair HP® en contacto con discos de dentina humana, que se obturaron y dividieron aleatoriamente para formar cuatro grupos: grupo 1 Biodentine™, grupo 2 MTA Repair HP®, grupo control positivo MTA Angelus® y grupo control negativo IRM®, los cuales se incubaron en solución PBS durante 10 días, para posterior análisis por medio de MEB-EDS y Espectroscopía Raman. Los tres materiales a base de silicato de calcio analizados en este estudio demostraron ser bioactivos pues al entrar en contacto con una solución a base de fosfato desencadenaron la precipitación inicial de fosfato de calcio amorfo, que actúa como precursor durante la formación de apatita carbonatada.