The purpose of this study was to evaluate if the bonding strength of dentin to dentin bonding agents increases with the application of a third layer of adhesive. 30 extracted molars were cut and embedded in acrylic before having the mid-dentin exposed with 600 grit SiC paper. Adhesives Prime&Bond NT, SingleBond 2 and Excite were applied, one group (n=5) received two layers of adhesive, as indicated by the manufacturer, and another group received a third layer of adhesive. Samples were stored in water for 7 days at 37º C before being tested in shear at a speed of 1 mm/min. Results in MPa were: PBNT 2 layers: 19.3; PBNT 3 layers: 32.6; SB2, 2 layers: 32.1; 3 layers: 38.2; EXC 2 layers: 38.2; EXC 3 layers: 44.7. The application of a third layer of adhesive increases the bond strength on dentin of the dentin bonding agents used in this studyl propósito de este estudio es evaluar si la aplicación de una tercera capa de adhesivo tiene algún efecto en la fuerza de adhesión de un adhesivo dentinal a la dentina. 30 piezas extraídas fueron cortadas y embebidas en acrílico, la dentina media fue expuesta con lija de SiC de grano 600; luego se aplicaron los adhesivos: Prime&Bond NT, SingleBond 2 y Excite. Un grupo (n=5) recibió dos capas de adhesivo, tal y como indica el fabricante, y el otro tres capas. Las muestras fueron probadas en cizalla luego de ser almacenadas 7 días en agua a 37º C, a una velocidad de 1 mm/min. Los resultados en MPa fueron: PBNT 2 capas: 19.3; PBNT 3 capas: 32.6; SB2, 2 capas: 32.1; SB2, 3 capas: 38.2; EXC 2 capas: 38.2; EXC 3 capas: 44.7. Así se concluye que una tercera capa de los adhesivos probados en este estudio, aumentan su fuerza de adhesión a dentina