Wood waste characterization for composting
Fecha
2009Registro en:
978-90-66056-52-7
2406-6168 (en línea)
0567-7572
Autor
Gonzalez, Joaquin
Del Pardo, Cecilia Karina
Martín, Susana
Resumen
Use of composted wood wastes has beneficial effects on soil physical and chemical conditions and on crop productivity. This paper includes compositional data from thirteen different wood industry wastes, including bark, chips, and sawdust from three Eucaliptus, Populus, and Salicaceae species, hardboard dust, mud from paper industry and raw cork. Particle size, pH and conductivity on the 1:10 waste:water extract, organic matter (ignition), organic C, total N, N-NO3, N-NH4, total Ca, Mg, K, Na, Cu, Mn, P, and Zn were determined. The C:N ratio was high in all of the materials (69 to 358), suggesting that it would be necessary to add N to help microorganisms to decompose the wastes. All wastes showed low N-NH4, P, Mg, K and Na content. N-NO3 varied from 259 to 829 ppm, with hardboard dust and mud from paper industry showing the highest values. Ca content was highest in the bark of the three species (1.91 to 5.60%). Cu content was highest (132 ppm) in mud from paper industry, while Zn was highest in the bark of Salicaceae species. The bark of Eucaliptus rostrata Schlecht and Eucaliptus saligna Smidth showed acceptable Mn content. This study shows that the different wood wastes tested are promising materials for composting and use in intensive cropping soils