The present work studies the behaviour of AISI 304, AISI 329 and AISI 420 stainless steels types under erosive wear. The three materials were submit to erosive wear with two particle impact speeds and four incidence angles. The test results show that the speed influence over the erosion for each steel. The behaviour of the stainless submits to erosion wear is defined by the structure of each one and impact speed of the impact particles. For a speed of 38 m/s and a impact angle of 45º and 90º, the lowest erosion resistance is shown by the AISI 420 stainless steel type, but for 60º and 90º impact angles, the lowest erosion resistance is shown by the AISI 329 stainless steel. . For 78 m/s impact speed, the lowest erosion resistance is shown by the AISI 329 stainless steel, independently of the particles impact angle.En el presente trabajo se estudia el comportamiento de los aceros inoxidables del tipo AISI 304, AISI 329 y AISI 420, ante el efecto del desgaste erosivo. Los tres materiales fueron sometidos a desgaste a dos velocidades de impacto de las partículas y a cuatro ángulos de incidencia de las mismas. Los resultados de los ensayos muestran la influencia de la velocidad sobre la intensidad del desgaste en cada uno de los aceros. El comportamiento de cada uno de los aceros ante el desgaste erosivo está definido por la estructura de cada una de ellos y las velocidades de impacto de las partículas erosivas. A la velocidad de 38 m/s y a los ángulos de incidencia de 300 y 450 la menor resistencia la muestra el acero AISI 420, pero a los valores comprendidos entre 600 y 900 la menor resistencia al desgaste la manifiesta el acero inoxidable austenítico. A la velocidad de 76 m/s la menor resistencia al desgaste la presenta el AISI 329, para cualquier valor del ángulo de incidencia.