Objective: Was to evaluate ex vivo the adaptation of conical fiber posts WhitePost DC 0,5 in circular canals prepared with the PostPrep 0.5 ultrasonic tip and WhitePost DC 0,5 drills. Materials and methods: 30 upper lateral incisors were used. The root canals were instrumented and apical filling. Subsequently, two experimental groups were randomly divided; Group 1 (15 roots): Post Preparation with PostPrep 0.5 ultrasonic tip and Group 2 (15 roots): prepared with WhitePost DC 0.5 drills. Conical fiberglass posts were cemented with resin cement. The roots were sectioned and cross sections were obtained from each root (Cervical third and apical third of the post). The cuts were observed with a Stereoscopic at 40x magnification. The adaptation of the post to the dentin walls could be measured, was evaluated the thickness of resinous cement and the area of the root canal occupied by the post. The statistical evaluation used the t-student and Mann-Whitney tests. Results: In the cervical thirds, a fine amount of dual resinous cement was obtained in both groups without difference between groups (p> .05) And a higher percentage of area occupied by the post in the root canal of 93.12% and 90.79% in both groups, and in the apical third of the post there was a smaller quantity of resinous cement for group 1 when com-pared with group 2 (p <.05), consequently a better adaptation of the post in the root canal. Likewise, the posts of group 1 presented a greater percentage of occupied area in the root canal 83.14% and 69.57% in group 2 with significant statistical difference between groups (p <0.5). Conclusions: In circular canals the ultrasonic preparation technique allowed a better adaptation of the conical fiberglass post in the canal, compared with rotary preparations.Objetivo: Evaluar ex vivo la adaptación de pernos de fibra cónicos WhitePost DC 0.5 en conductos circulares preparados con la punta ultrasónica PostPrep 0.5 y la fresa WhitePost DC 0.5. Materiales y métodos: 30 incisivos laterales superio-res fueron seleccionados, instrumentados y obturados solamente los tercios apicales. Posteriormente se procedió a dividir aleatoriamente en dos grupos experimentales de acuerdo al tipo de preparación del espacio para retención intrarradicular, siendo Grupo 1 (15 raíces): preparación con la punta ultrasónica PostPrep 0.5 y Grupo 2 (15 raíces): preparados con la fresa WhitePost DC 0.5. Se cementaron los pernos en ambos grupos con cemento resinoso dual. Se obtuvieron cortes transversa-les de cada raíz (tercio cervical y tercio apical del perno). Los cortes fueron observados con una lupa estereoscópica a 40x. Se pudo medir la adaptación del poste a las paredes dentinarias, donde se evaluó la espesura de cemento resinoso y el área del conducto ocupado por el perno. Las pruebas estadísticas utilizadas fueron de t-student y U Mann-Whitney con un nivel de significancia de 5%. Resultados: En los tercios cervicales se obtuvo una fina cantidad de cemento resinoso en ambos grupos sin diferencia entre grupos (p>0.05) y un alto porcentaje de área ocupada por el perno en el conducto radicular de 93,12% y 90,79% en los grupos respectivos, ya en el tercio apical del perno se tuvo una menor cantidad de cemento resino-so para el grupo 1 comparado con el grupo 2 (p<0.05), consecuentemente una mejor adaptación del perno en el conducto. Así mismo, los pernos del grupo 1 presentaron un mayor porcentaje de área ocupada en el conducto radicular 83,14% y 69,57% en el grupo 2, con diferencia estadísticamente significativa entre grupos (p<0.05). Conclusiones: En conductos circulares, en el tercio apical, la técnica de preparación ultrasónica permitió una mejor adaptación y mayor área ocupada por el perno de fibra de vidrio cónico en el conducto cuando comparada con preparaciones rotatorias.