Thermal stability of ionene polymers
Date
2013-06-01Registration in:
Journal of Thermal Analysis and Calorimetry, v. 112, n. 3, p. 1221-1229, 2013.
1388-6150
10.1007/s10973-012-2694-7
WOS:000319358500011
2-s2.0-84878711444
Author
Universidade Estadual Paulista (Unesp)
Federal University of Rio de Janeiro
Universidade de São Paulo (USP)
UNIFIEO
Abstract
Two different cationic polymers of the same chemical type and with very similar chemical structures were reacted with a natural bentonite over a wide range of polymer/clay ratios. This study involved the synthesis of cationic aliphatic ammonium polyionenes, specifically 3,6-ionene and 3,6-dodecylionene. Ionenes are ion-containing polymers that contain quaternary nitrogen atoms in the main macromolecular chain as opposed to a pendant chain. The CHN content, basal spacing, and elemental composition of each of the polymer-clay complexes were analyzed by X-ray diffraction, X-ray fluorescence, and thermogravimetry. All the polycations reacted to form interlayer complexes with clay, which displaced more Na+ and little Ca2+. Sodium and calcium were both present as interlayer cations in the clay and its complexes. The TG/DTG curves show that both polymers underwent thermal degradation in more than one stage. Specifically, 3,6-ionene was found to undergo two stages of decomposition and 3,6-dodecylionene undergo three stages. The behavior of the TG/DTG curves and the activation energy values suggest that 3,6-dodecylionene (E = 174,85 kJ mol-1) complexes have greater thermal stability than 3,6-ionene (E = 115,52 kJ mol-1) complexes. The mechanism of degradation suggests a direct interaction with the dodecyl chain containing 12 carbons, which are present in 3,6-dodecylionene but not in 3,6-ionene. © 2012 Akadémiai Kiadó, Budapest, Hungary.
Subjects
Related items
Showing items related by title, author, creator and subject.
-
Self-organization and swelling of ruthenium-metal coordination polymers with PTA (metal = Ag, Au, Co)
Sierra-Martin B.; Serrano-Ruiz M.; García-Sakai V.; Scalambra F.; Romerosa A.; Fernandez-Barbero A. (MDPI AG, 2018) -
Thermally Promoted Elimination and Substitution Reactions in Poly(p-arylene vinylene) Precursor Polyelectrolytes
Garay, Raúl Oscar; Sarimbalis, Myrian N.; Hernandez, Sandra Analia; Montani, Rosana Silvia (American Chemical Society, 2000-06)The thermal conversion of dialkylsulfonium polyelectrolyte precursor polymers 1b-e to poly(p-arylene vinylene)s was studied by direct pyrolysis mass spectrometry in order to elucidate the mechanism of the sulfonium elimination ... -
New thiophene-based poly(azomethine)s bearing tetraphenylsilane moieties along their backbone. Optical, electronic, thermal properties and theoretical calculations
Sobarzo P.A.; Jessop I.A.; Mariman A.P.; González A.F.; Saldías C.; Schott E.; Zarate X.; Hauyon R.A.; Recabarren-Gajardo G.; González-Henríquez C.M.; Tundidor-Camba A.; Terraza C.A. (Elsevier Ltd, 2020)