Iron Insertion And Hematite Segregation On Fe-doped Tio 2 Nanoparticles Obtained From Sol-gel And Hydrothermal Methods
Registro en:
Acs Applied Materials And Interfaces. , v. 4, n. 10, p. 5555 - 5561, 2012.
19448244
10.1021/am301444k
2-s2.0-84867812415
Autor
Santos R.D.S.
Faria G.A.
Giles C.
Leite C.A.P.
Barbosa H.D.S.
Arruda M.A.Z.
Longo C.
Institución
Resumen
Iron-doped TiO 2 (Fe:TiO 2) nanoparticles were synthesized by the sol-gel method (with Fe/Ti molar ratio corresponding to 1, 3, and 5%), followed by hydrothermal treatment, drying, and annealing. A similar methodology was used to synthesize TiO 2 and α-Fe 2O 3 nanoparticles. For comparison, a mixture hematite/titania, with Fe/Ti = 4% was also investigated. Characterization of the samples using Rietveld refinement of X-ray diffraction data revealed that TiO 2 consisted of 82% anatase and 18% brookite; for Fe:TiO 2, brookite increased to 30% and hematite was also identified (0.5, 1.0, and 1.2 wt % for samples prepared with 1, 3, and 5% of Fe/Ti). For hematite/titania mixture, Fe/Ti was estimated as 4.4%, indicating the Rietveld method reliability for estimation of phase composition. Because the band gap energy, estimated as 3.2 eV for TiO 2, gradually ranged from 3.0 to 2.7 eV with increasing Fe content at Fe:TiO 2, it can be assumed that a Fe fraction was also inserted as dopant in the TiO 2 lattice. Extended X-ray absorption fine structure spectra obtained for the Ti K-edge and Fe K-edge indicated that absorbing Fe occupied a Ti site in the TiO 2 lattice, but hematite features were not observed. Hematite particles also could not be identified in the images obtained by transmission electron microscopy, in spite of iron identification by elemental mapping, suggesting that hematite can be segregated at the grain boundaries of Fe:TiO 2. © 2012 American Chemical Society. 4 10 5555 5561 Chen, X., Mao, S.S., (2007) Chem. Rev., 107, p. 2891 Grätzel, M., (2003) Photochem. Photobiol. C, 4, p. 145 Longo, C., De Paoli, M.-A., (2003) J. Braz. Chem. Soc., 14, p. 889 Hagfeldt, A., Boschloo, G., Sun, L., Kloo, L., Pettersson, H., (2010) Chem. Rev., 110, p. 6595 Liu, Z., Li, Y., Li, C., Ya, J., Lei, E., Zhao, W., Zhao, D., Na, L., (2011) ACS Appl. Mater. Interfaces, 3, p. 1721 Lee, H., Hwang, D., Jo, S.M., Kim, D., Seo, Y., Kim, D.Y., (2012) ACS Appl. Mater. Interfaces, 4, p. 3308 Walter, M.G., Warren, E.L., McKone, J.R., Boettcher, S.W., Mi, Q., Santori, E.A., Lewis, N.S., (2010) Chem. Rev., 110, p. 6446 Fujishima, A., Zhang, X., Tryk, D.A., (2008) Surf. Sci. Rep., 63, p. 515 Oliveira, H.G., Nery, D.C., Longo, C., (2010) Appl. Catal., B, 93, p. 205 Akpan, U.G., Hameed, B.H., (2010) Appl. Catal., A, 375, p. 1 Asahi, R., Morikawa, T., Ohwaki, T., Aoki, K., Taga, Y., (2001) Science, p. 269 Choi, J., Park, H., Hoffmann, M., (2010) J. Phys. Chem. C, 114, p. 783 Kachina, A., Puzenat, E., Ould-Chikh, S., Geantet, C., Delichere, P., Afanasiev, P., (2012) Chem. Mater., 24, p. 636 Zhang, J., Pan, C., Fang, P., Wei, J., Xiong, R., (2010) ACS Appl. Mater. Interfaces, 2, p. 1173 Liu, H., Wu, Y., Zhang, J., (2011) ACS Appl. Mater. Interfaces, 3, p. 1757 Pulsipher, D.I., Martin, I.T., Fisher, E.R., (2010) ACS Appl. Mater. Interfaces, 2, p. 1743 Zhu, S., Shi, T., Liu, W., Wei, S., Xie, Y., Fan, C., Li, Y., (2007) Phys. B, 396, p. 177 Qingping, W., Van De Krol, R., (2012) J. Am. Chem. Soc., 134, p. 9369 Wang, X.H., Li, J.-G., Kamiyama, H., Moriyoshi, Y., Ishigaki, T., (2006) J. Phys Chem B, 110, p. 6804 Santos, R.S., Oliveira, H.G., Longo, C., (2009) Proceedings of SPIE: Solar Hydrogen and Nanotechnology IV, 7408, pp. 74080O. , Osterloh, F. E. International Society for Optics and Photonics: Bellingham, WA Sonawane, R.S., Kale, B.B., Dongare, M.K., (2004) Mater. Chem. Phys., 85, p. 52 Piera, E., Tejedor-Tejedor, M.I., Zorn, M.E., Anderson, M.A., (2003) Appl. Catal., B, 46, p. 671 Colemenares, J.C., Aramendia, M.A., Marinas, A., Marinas, A., Urbano, F., (2006) J. Appl. Catal. A, 306, p. 120 Yang, M., Hume, C., Lee, S., Son, Y.H., Lee, J.K., (2010) J. Phys. Chem. C, 114, p. 15292 Young, K.F., Frederikse, H.P.R., (1973) J. Phys. Chem. Ref. Data, 2, p. 313 Wang, J.A., Limas-Ballesteros, R., Lopez, T., Moreno, A., Gomez, R., Novaro, O., Bokhimi, X., (2001) J. Phys. Chem. B, 105, p. 9692 Litter, M.I., Navío, J.A., (1996) J. Phochem. Photobiol. A, 98, p. 171 Li, X., Yue, P.L., Kutal, C., (2003) New J. Chem., 27, p. 1264 Huo, L., Li, Q., Zhao, H., Yu, L., Gao, S., Zhao, J., (2005) Sens. Actuators B, 107, p. 915 Wang, X.H., Li, J.-G., Kamiyama, H., Katada, M., Ohashi, N., Moriyoshi, Y., Ishigaki, T., (2005) J. Am. Chem. Soc., 127, p. 10982 Larson, A.C., Von Dreele, R.B., (1994) LANL Report LAUR 86-748: General Structure Analysis System (GSAS), , Los Alamos National Laboratory: Los Alamos, NM Toby, B.H., (2001) J. Appl. Crystallogr., 34, p. 210 Bokimi, X., Morales, A., Novaro, O., Lopéz, T., Gomez, R., (1995) J. Mater. Res., 10, p. 2788 Young, R.A., (1993) The Rietveld Method, , Oxford University Press: New York Azimov, P.Y., Bushmin, S.A., (2007) Geochem. Int., 45, p. 1210 Shannon, R.D., (1976) Acta Crystallogr., 32, p. 751 Colon, G., Hidalgo, M.C., Munuera, G., Ferino, I., Cutrufello, M.G., Navio, J.A., (2006) Appl. Catal., B, 63, p. 45 Ambrus, Z., Balázs, N., Alapi, T., Wittmann, G., Sipos, P., Dombi, A., Mogyorósi, K., (2008) Appl. Catal., B, 81, p. 27 Farges, F., Bronw, G.E., Rehr, J., (1997) J. Phys. Rev. B, 56, p. 1809 Angelomé, P.A., Andrini, L., Calvo, M.E., Requejo, F.G., Bilmes, S.A., Soler-Illia, G.J.A.A., (2007) J. Phys. Chem. C, 111, p. 10886 Vasiliu, F., Diamandescu, L., MacOvei, D., Teodorescu, C.M., Nicula, R., (2009) J. Mater. Sci: Mater. Electron, 20, p. 211 Djerdj, I., Tonejc, A.M., (2006) J. Alloys Compd., 413, p. 159 Diamandescu, L., Vasiliu, F., Tarabasanu-Mihaila, D., Feder, M., Vlaicu, A.M., Teodorescu, C.M., MacOvei, D., Vasile, E., (2008) Mater. Chem. Phys., 112, p. 146 Carp, O., Huisman, C.L., Reller, A., (2004) Prog. Solid State Chem., 32, p. 33