Effect of CaO on the microsture and non-ohmic properties of (Co, Sb)-doped SnO2 vatistors

Effect of CaO on the microsture and non-ohmic properties of (Co, Sb)-doped SnO2 vatistors

dc.contributores-ES
dc.contributoren-US
dc.creatorCastillo Torres, J.
dc.creatorHernández, M. B.
dc.creatorAguilar Martínez, J. A.
dc.creatorPech Canul, M. I.
dc.creatorDurán Regules, A.
dc.creatorGlot, A. B.
dc.date2009-10-05
dc.date.accessioned2018-03-16T15:47:02Z
dc.date.available2018-03-16T15:47:02Z
dc.identifierhttp://ojs.unam.mx/index.php/rmf/article/view/14303
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/1202411
dc.descriptionSe investigó el efecto del CaO a través de adiciones de CaCO3 sobre las características físicas, la microestructura y las propiedades corriente-voltaje de varistores de SnO2 dopados con Co y Sb. Los cerámicos SnO2-Co3O4-Sb2O5 dopados con 0.1, 0.5 y 1% molar de CaO fueron sinterizados a 1450 ºC bajo condiciones oxidantes y caracterizados por microscopía electrónica de barrido (MEB), espectroscopía por energía dispersiva de rayos X (EDX) y por difracción de rayos X (DRX). Los resultados muestran que, a niveles bajo e intermedio de CaO, la densidad no se ve afectada significativamente mientras que al nivel más alto, la densidad disminuye sustancialmente. El coeficiente de no linealidad y el voltaje de ruptura se comportan en un sentido de manera similar, porque ambos presentan un máximo y porque al nivel más alto de CaO ambos presentan los valores más bajos. El coeficiente de no linealidad presenta un máximo de 12.9 a 0.1% molar de CaO, mientras que el máximo correspondiente para el voltaje de ruptura ocurre a 0.5% molar de CaO. A 1% molar de CaO, El voltaje de ruptura es de 288 V cm-1.es-ES
dc.descriptionThe effect of CaO through additions of CaCO3 on the physical characteristics, microstructure, and current-voltage properties of (Co-Sb)- doped SnO2 varistors was investigated. SnO2-Co3O4-Sb2O5 ceramics with additions of 0.1, 0.5 and 1 mol % CaO were sintered at 1450ºC under oxidizing atmosphere and characterized by scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), and X-ray diffraction (XRD). Results show that, at low and intermediate CaO levels, density is not significantly influenced, whilst at the highest level, density decreases substantially. The nonlinear coefficient and the breakdown voltage behave similarly in one sense because both present a maximum, and because at the highest CaO level, both response variables show the lowest values. The nonlinear coefficient presents a maximum of 12.9 at 0.1 mol % CaO, while the same maximum for the breakdown voltage occurs at 0.5 mol % CaO. at 1 mol % CaO, The breakdown voltage is 288 Vcm-1.en-US
dc.formatapplication/pdf
dc.languagespa
dc.publisherRevista Mexicana de Físicaes-ES
dc.relationhttp://ojs.unam.mx/index.php/rmf/article/view/14303/13640
dc.sourceRevista Mexicana de Física; Vol 54, No 001 (2008)es-ES
dc.subjectVaristores; voltaje de ruptura; no linealidades-ES
dc.subjectVaristors; breakdown voltage; nonlinearityen-US
dc.titleEffect of CaO on the microsture and non-ohmic properties of (Co, Sb)-doped SnO2 vatistorses-ES
dc.titleEffect of CaO on the microsture and non-ohmic properties of (Co, Sb)-doped SnO2 vatistorsen-US