Modeling Vinyl Acetate and n-Butyl Acrylate Emulsion Copolymerization Process
(WILEY-BLACKWELL, 2010)
This work presents a mathematical model for the vinyl acetate and n-butyl acrylate emulsion copolymerization process in batch reactors. The model is able to explain the effects of simultaneous changes in emulsifier ...
Kinetic parameters obtained for thermal decomposition of acrylic resins present in commercial paint emulsions
(Springer, 2007-06-01)
Samples of water based commercial acrylic resin paints were spread in a film form on slides, dried at room temperature and exposed to solar radiation for up to eight months.The characterization and quantification of resins ...
Kinetic parameters obtained for thermal decomposition of acrylic resins present in commercial paint emulsions
(Springer, 2007-06-01)
Samples of water based commercial acrylic resin paints were spread in a film form on slides, dried at room temperature and exposed to solar radiation for up to eight months.The characterization and quantification of resins ...
Synthesis and characterization of a pressure-sensitive adhesive based on an isobutyl acrylate / 2-ethylhexyl acrylate copolymer
(De Gruyter OpenCiencia de los MaterialesFrancia, 2022)
Molecular Characterization of Alkyd/Acrylic Latexes Prepared by Miniemulsion Polymerization
(John Wiley & Sons Inc, 2009-05)
The molecular characterization of alkyd/ acrylic hybrid latexes produced by miniemulsion polymerization was characterized in terms of the resin degree of grafting, acrylic degree of grafting, reacted double bonds in the ...
Síntesis y evaluación de adhesivos sensibles a la presión Núcleo-Coraza vía polimerización en emulsión y mini emulsión
(2018-05-07)
RESUMEN:
Síntesis de látex poliméricos se obtuvieron mediante polimerización en emulsión y mini emulsión vía proceso semicontinuo. La síntesis realizada por etapas partió de la síntesis de una semilla vía batch, seguido ...
Polyurethane/Acrylate Hybrids: Effects of the Acrylic Content and Thermal Treatment on the Polymer Properties
(John Wiley & Sons IncHobokenEUA, 2010)