The viscoelastic properties of nanocomposites based on epoxy and epoxy-phenolic blend matrix reinforced with multi wall-carbon nanotubes were studied. It was varied the content of carbon nanotube (0.2 and 0.5 wt.%) and ...

The curing reaction of an epoxy-phenolic resin under different conditions was monitored using rheological measurements. The evolution of viscoelastic properties, such as storage modulus, G′, and loss modulus, G″, was ...

An epoxy-phenolic resin suitable for use as a composite matrix was reinforced with modified nanoclay (montmorillonite type). Characterization by x-ray diffraction and transmission electron microscopy (TEM) demonstrated ...

Epoxy-amine was blended with two resol resins to study the influence of the fined network and void content on the water absorption of these systems. To characterize the network structure of the blends, infrared analyses ...

The aim of the present research was to evaluate the physical and mechanical properties of LVL reinforced with fiberglass with two types of resins. Pinus elliottii veneers with 1,5 mm thickness were used to manufacture ...

Liquid and cured epoxy-phenolic lacquers used as can coatings were characterized. Tinplate was used as the base material, which was coated with lacquers of different epoxy to phenolic ratios (EPRs) from a commercial source. ...

The influence of different factors on the miscibility of diglycidyl ether of bisphenol A (DGEBA)/thermoplastic blends was studied. DGEBA/poly(ether imide) (PEI) blends exhibited upper critical solution temperature behavior. ...

Se estudió la relación entre la estructura química de resoles con distinta relación molar formaldehído/fenol (F/Ph) y las propiedades mecánicas, con la resistencia a la temperatura. Los resoles que muestran una mayor ...

This project studies the formulation of an epoxy system for use in artistic encapsulation applications, with eye-catching and customized finishes. The motivation stems from the need to solve some of the problems of epoxy ...