Evaluation of an electroless nickel interlayer on the fatigue & corrosion strength of chromium-plated AISI 4340 steel
(Amer Electroplaters Soc Inc, 2001-04-01)
Despite the fact that chromium electrodeposition results in protection against wear and corrosion, combined with chemical resistance and good lubricity, the reduction in fatigue strength of base metal and environmental ...
Evaluation of an electroless nickel interlayer on the fatigue & corrosion strength of chromium-plated AISI 4340 steel
(Amer Electroplaters Soc Inc, 2001-04-01)
Despite the fact that chromium electrodeposition results in protection against wear and corrosion, combined with chemical resistance and good lubricity, the reduction in fatigue strength of base metal and environmental ...
Effects of surface treatments on the fatigue strength of AISI 4340 aeronautical steel
(Elsevier B.V., 2001-08-01)
Internal residual stresses significantly influence the fatigue strength of coated materials. It is well known that chromium plating is the most used electrodeposited coating for important industrial applications. However, ...
Effects of surface treatments on the fatigue strength of AISI 4340 aeronautical steel
(Elsevier B.V., 2001-08-01)
Internal residual stresses significantly influence the fatigue strength of coated materials. It is well known that chromium plating is the most used electrodeposited coating for important industrial applications. However, ...
An investigation of electrolytic surface damages and electroplated crhomium effects on fatigue behavior of high strength steel
(2001-12-01)
Fatigue crack initiation occurs at the surface, although sub surface nucleation has also been reported. Localized imperfections like inclusions close to surface and surface small pits can result in crack sources. Coatings ...
An investigation of electrolytic surface damages and electroplated crhomium effects on fatigue behavior of high strength steel
(2001-12-01)
Fatigue crack initiation occurs at the surface, although sub surface nucleation has also been reported. Localized imperfections like inclusions close to surface and surface small pits can result in crack sources. Coatings ...
Residual stress influence on fatigue lifetimes of electroplated AISI 4340 high strength steel
(Blackwell Publishing, 2007-11-01)
Residual stresses play an important role in the fatigue lives of structural engineering components. In the case of near surface tensile residual stresses, the initiation and propagation phases of fatigue process are ...
Residual stress influence on fatigue lifetimes of electroplated AISI 4340 high strength steel
(Blackwell Publishing, 2007-11-01)
Residual stresses play an important role in the fatigue lives of structural engineering components. In the case of near surface tensile residual stresses, the initiation and propagation phases of fatigue process are ...