Extrusion-cooking of cassava starch as a pre-treatment for its simultaneous saccharification and fermentation for ethanol production
Registro en:
Acta Alimentaria. Akademiai Kiado, v. 32, n. 3, n. 219, n. 235, 2003.
0139-3006
WOS:000185838400002
10.1556/AAlim.32.2003.3.2
Autor
Chang, YK
El-Dash, AA
Institución
Resumen
Single screw extrusion of cassava starch was evaluated as a pre-treatment for the enzymatic hydrolysis of the extrudate and fermentation to yield alcohol. The acid concentration, barrel temperature and moisture content showed that all the variables were significant. Increasing acid concentration or barrel temperature induced starch depolymerisation with a higher water solubility index and lower water absorption index. At 20 and 24% moisture contents the cold paste viscosity decreased. As a result of the addition of acid during extrusion cooking the degree of starch hydrolysis resulted in low hot paste viscosity. Acid concentration was significant in the production of reducing sugars. At concentrations above 0.024 N, as the temperature increased, the reducing sugar content also increased. Nevertheless, at concentrations below 0.024 N, the reducing sugar content showed the opposite result. The best yield of alcohol obtained from the extruded starch was 98.7% (0.56 g of ethanol/g starch), which, on average, was 5.7% and 6.8% higher than that obtained from starch extruded without acid and from starch gelatinized by the conventional method, respectively. 32 3 219 235