dc.contributor | Medina Carbajal, Lucio Sigifredo | |
dc.creator | Rodríguez Menéndez, Diana Priscila | |
dc.creator | Rodríguez Menéndez, Diana Priscila | |
dc.creator | Gutiérrez Acuña, Edward Ramiro | |
dc.date.accessioned | 2024-02-12T21:40:14Z | |
dc.date.accessioned | 2024-05-16T15:17:38Z | |
dc.date.available | 2024-02-12T21:40:14Z | |
dc.date.available | 2024-05-16T15:17:38Z | |
dc.date.created | 2024-02-12T21:40:14Z | |
dc.date.issued | 2024 | |
dc.identifier | https://hdl.handle.net/20.500.12759/21231 | |
dc.identifier.uri | https://repositorioslatinoamericanos.uchile.cl/handle/2250/9480073 | |
dc.description.abstract | La presente tesis se desarrolló en Trujillo, planteando como objetivo principal la
evaluación al adicionar filler calizo sobre la pérdida de trabajabilidad y parámetros
de resistencia del concreto; llegándose a ejecutar una metodología cuantitativa y
experimental basada en el análisis de una muestra constituida por 200
especímenes cilíndricos y 30 vigas distribuidas en edades de evaluación de 3, 7,
28 y 56 días de curado para el caso de resistencia a la compresión; y, 28 y 56 días
para resistencia a la flexión, considerando un concreto patrón y 4 concretos
experimentales correspondientes a dosis de 5%, 10%, 15% y 20% de reemplazo
del cemento por filler calizo, todos proyectados para un f’c de 210kg/cm2; cuyos
resultados evidencian que la trabajabilidad mejora en función del incremento de la
dosis utilizada; mientras que, la resistencia a la compresión y flexión tienen a
disminuir progresivamente en función al porcentaje de reemplazo; sin embargo, al
5% y 10% se supera la resistencia de diseño en compresión; además, con 5%
incrementa el módulo de rotura respecto al concreto patrón; por lo que se concluye
que, el porcentaje óptimo es de 5%, ya que supera la resistencia de diseño en
cuanto a compresión, mejora la resistencia a la flexión y ofrece más trabajabilidad
en estado fresco | |
dc.description.abstract | This thesis was developed in Trujillo, with the main objective being the evaluation
of the loss of workability and strength parameters of concrete when adding
limestone filler; leading to the execution of a quantitative and experimental
methodology based on the analysis of a sample consisting of 200 cylindrical
specimens and 30 beams distributed at evaluation ages of 3, 7, 28 and 56 days of
curing in the case of compression resistance; and, 28 and 56 days for flexural
strength, considering a standard concrete and 4 experimental concretes
corresponding to doses of 5%, 10%, 15% and 20% replacement of cement with
limestone filler, all projected for a f'c 210kg/cm2; whose results show that workability
improves depending on the increase in the dose used; while, the resistance to
compression and flexion tend to decrease progressively depending on the
replacement percentage; However, at 5% and 10% the design resistance in
compression is exceeded; Furthermore, with 5% the modulus of rupture increases
with respect to the standard concrete; Therefore, it is concluded that the optimal
percentage is 5%, since it exceeds the design resistance in terms of compression,
improves flexural resistance and offers more workability in the fresh state. | |
dc.language | spa | |
dc.publisher | Universidad Privada Antenor Orrego | |
dc.publisher | PE | |
dc.relation | T_CIVIL_2473 | |
dc.rights | https://creativecommons.org/licenses/by/4.0/ | |
dc.rights | info:eu-repo/semantics/closedAccess | |
dc.subject | Concreto | |
dc.title | Evaluación de la adición de filler calizo en la pérdida de trabajabilidad yparámetros de resistencia de concreto, Trujillo 2023 | |
dc.type | info:eu-repo/semantics/bachelorThesis | |