Preparação e caracterização de materiais híbridos celulose/NbOPO4.nH2O a partir de celulose branqueada de bagaço de cana-de-açúcar

dc.contributorUniversidade Estadual Paulista (UNESP)
dc.creatorPereira, Paulo H. F.
dc.creatorVoorwald, Herman Jacobus Cornelis
dc.creatorCioffi, Maria O. H.
dc.creatorPereira, Maria L. C. P. da S.
dc.date2014-05-20T15:15:57Z
dc.date2016-10-25T21:21:18Z
dc.date2014-05-20T15:15:57Z
dc.date2016-10-25T21:21:18Z
dc.date2012-01-01
dc.date.accessioned2017-04-06T09:22:26Z
dc.date.available2017-04-06T09:22:26Z
dc.identifierPolimeros-Ciência e Tecnologia. São Carlos: Assoc Brasil Polimeros, v. 22, n. 1, p. 88-95, 2012.
dc.identifier0104-1428
dc.identifierhttp://hdl.handle.net/11449/130495
dc.identifierhttp://acervodigital.unesp.br/handle/11449/130495
dc.identifier10.1590/S0104-14282012005000002
dc.identifierS0104-14282012000100015
dc.identifierWOS:000302850900015
dc.identifierS0104-14282012000100015.pdf
dc.identifierhttp://dx.doi.org/10.1590/S0104-14282012005000002
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/941038
dc.descriptionEste trabalho descreve a preparação e caracterização do híbrido celulose/fosfato de nióbio hidratado (Cel/NbOPO4.nH2O) utilizando como material de partida a celulose branqueada de bagaço de cana-de-açúcar e o nióbio metálico. O híbrido foi preparado por dois métodos: denominados métodos I e II. O método I consistiu na dissolução do nióbio metálico em solução de ácido fluorídrico/nítrico (100:10), com tempo de contato de 16 horas entre a celulose branqueada do bagaço de cana-de-açúcar e a solução ácida. Adicionou-se a essa solução ácido fosfórico para precipitação do material. O método II foi semelhante, com proporções diferentes da solução ácida fluorídrico/nítrico (160/100), sem tempo de contato da celulose com a solução ácida. Os métodos I e II utilizaram as seguintes proporções de cel/ Nb2O5.nH2O: (10:10);(10:6) e (10:2). Os materiais preparados pelos métodos I e II foram caracterizados por difração de raios X (DRX), termogravimetria (TG/DTG) e microscopia eletrônica de varredura (MEV). Observou-se aumento do índice do grau de cristalinidade e mudanças na morfologia dos materiais preparados.
dc.descriptionThis work describes the preparation and characterization of cellulose/hydrous niobium phosphate hybrid with bleached cellulose from sugarcane bagasse. The hybrid was prepared in two different forms: named methods I and II. Method I consisted in dissolving metallic niobium in a fluoridric/nitric (100:10) mixture, with aging time of 16 hours in which the sugarcane bagasse was in contact with the acid solution. Phosphoric acid was then added to the solution for precipitation of the material. Method II was similar, but metallic niobium was diluted in a fluoridric /nitric (160/100) solution without aging time. In both methods different proportions of Cel/NbOPO4.nH2O were used: (10:10); (10:6) and (10:2). These materials were characterized by X-ray diffraction (XRD), thermogravimetry (TG/DTG) analysis and scanning electronic microscopy (SEM). The deposition of niobium phosphate and an increase in crystallinity were observed.
dc.descriptionFundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
dc.languagepor
dc.publisherAssociação Brasileira de Polímeros
dc.relationPolímeros
dc.rightsinfo:eu-repo/semantics/openAccess
dc.subjectBagaço de cana-de-açúcar
dc.subjecthíbrido orgânico-inorgânico
dc.subjectfosfato de nióbio hidratado
dc.subjectSugarcane bagasse
dc.subjectorganic-inorganic hybrid
dc.subjecthydrous phosphate niobium
dc.titlePreparação e caracterização de materiais híbridos celulose/NbOPO4.nH2O a partir de celulose branqueada de bagaço de cana-de-açúcar
dc.typeOtro


Este ítem pertenece a la siguiente institución