| dc.description | En el presente trabajo se describe el proceso de síntesis del marco de imidazolato zeolítico 67 (ZIF-67) policristalino, en el cual se empleó la técnica de hand-milling y de lavado por centrifugación. El análisis por difracción de rayos X muestran que el ZIF-67 posee una estructura cristalina tipo cúbica centrada en el cuerpo de parámetro de red de 17.01 Å tipo armazón. El análisis de área superficial y porosimétrico arrojan que ZIF-67 posee un tamaño de poro promedio de 1.6 nm y un área superficial específica de 1966.37 m²/g. Se estudió la filtración a través del ZIF-67 de una suspensión extraída de una muestra de suelo de la zona de relave de la planta piloto concentradora de la FIGMM-UNI, cuyo análisis por plasma de acoplamiento inductivo arroja que el compuesto sintetizado tiene la capacidad de adsorber un promedio de 94% de los diferentes elementos presentes en la suspensión, además, se evidencia la disolución parcial de ZIF-67 en este proceso. | |
| dc.description | In this work, we described the synthesis process of the polycrystalline zeolitic imidazolte framework 67 (ZIF-67), in which it was used the technique of hand milling and centrifugal washing. X-ray diffraction analysis shows that ZIF-67 possesses a body centred cubic-like crystalline structure with a lattice parameter 17.01 Å. The BET analysis shows the average size of porous in ZIF-67 is 1.6 nm and it has a specific superficial area of 1966.37 m²/g. We studied the filtration through ZIF-67 of a suspension extracted from a soil sample from the tailings zone of the FIGMM-UNI’s pilot plant. The analysis by inductively coupled plasma (ICP) shows the synthesized compound has the average capacity of adsorption of 94% of different elements from the suspension; furthermore, the presence of cobalt in the filtered simple evidences the partially decomposition about ZIF-67 in this process. | |
| dc.description | Tesis | |
| dc.format | application/pdf | |
| dc.language | spa | |
| dc.publisher | Universidad Nacional de Ingeniería | |
| dc.publisher | PE | |
| dc.rights | info:eu-repo/semantics/openAccess | |
| dc.rights | http://creativecommons.org/licenses/by-nc-nd/4.0/ | |
| dc.source | Universidad Nacional de Ingeniería | |
| dc.source | Repositorio Institucional - UNI | |
| dc.subject | Método de Hand Milling | |
| dc.subject | Marco de imidazolato zeolítico 67 | |
| dc.subject | http://purl.org/pe-repo/ocde/ford#1.03.01 | |
| dc.title | Síntesis y caracterización estructural del marco de imidazolato zeolítico 67 por el método de Hand Milling | |
| dc.type | info:eu-repo/semantics/masterThesis | |