dc.creator | GROSSO, R.L. | |
dc.creator | REIS, S.L. | |
dc.creator | MUCCILLO, E.N.S. | |
dc.creator | EUROPEAN MATERIALS RESEARCH SOCIETY SPRING MEETING AND EXHIBIT | |
dc.date | 2017-07-04T12:02:34Z | |
dc.date | 2017-07-04T12:02:34Z | |
dc.date | May 2-6, 2016 | |
dc.date.accessioned | 2023-09-28T13:34:21Z | |
dc.date.available | 2023-09-28T13:34:21Z | |
dc.identifier | http://repositorio.ipen.br/handle/123456789/27601 | |
dc.identifier.uri | https://repositorioslatinoamericanos.uchile.cl/handle/2250/8997865 | |
dc.description | The electrical conductivity and the crystalline structure of zirconia-10 mol% scandia-x
mol% niobia solid electrolytes were investigated for x=0.25, 0.50 and 1.00 mol%. Dense
specimens with relative densities higher than 95% were obtained by solid state reaction and
sintering at 1500??C for 5 h. Full stabilization of the cubic structure at room temperature was
obtained for compositions with x=0.50 and 1.00, whereas for x=0.25 cubic and rhombohedric
structures coexist. The electrical conductivity determined by impedance spectroscopy is of the
same order of magnitude as that of the parent solid electrolyte (zirconia-10 mol% scandia) in the
high temperature range (above 600??C). The isothermal conductivity of the solid electrolyte with
x=0.50 mol% niobium oxide remains constant up to 100 h at 600??C. | |
dc.rights | openAccess | |
dc.title | Enhanced electrical conductivity of zirconia-scandia with niobia addition | |