Fe K-edge X-ray absorption spectroscopy study of Pb(Fe2/3W 1/3)O3-PbTiO3 multiferroic ceramics
Journal of Applied Physics, v. 113, n. 11, 2013.
Fraygola, B. M.
Mastelaro, V. R.
Eiras, J. A.
The present paper is a comprehensive study concerning Fe K-edge X-ray absorption spectroscopy (XAS) measurements, which were performed to characterize the local structure of (1 - x)Pb(Fe2/3W1/3)O 3-xPbTiO3 samples as a function of temperature and PbTiO3 content. Results obtained by the fits of extended X-ray absorption fine structure consist with rhombohedral symmetry for Pb(Fe 2/3W1/3)O3 composition at temperatures lower than room temperature. This result is in apparent disagreement with X-ray and neutron diffraction characterization which have been reported. This apparent disagreement is related to the fact that XAS probes the short-range order, whereas X-ray diffraction provides structural information about the average structure. Moreover, as the PbTiO3 content increases, a disorder has been detected at local structure of the FeO6 octahedron. Analysis of X-ray absorption near edge structure spectra did not show modifications in intensity nor energy of transitions. © 2013 American Institute of Physics.
Showing items related by title, author, creator and subject.
Local electronic structure, optical bandgap and photoluminescence (PL) properties of Ba(Zr0.75Ti0.25)O3 powders Cavalcante, L. S.; Batista, N. C.; Badapanda, T.; Costa, M. G S; Li, M. S.; Avansi, W.; Mastelaro, V. R.; Longo, Elson; Espinosa, J. W M; Gurgel, M. F C
Local electronic structure, optical bandgap and photoluminescence (PL) properties of Ba(Zr0.75Ti0.25)O3 powders Universidade Estadual do Piauí (UESPI); Universidade Estadual Paulista (UNESP); National Institute of Technology; Química; Universidade de São Paulo (USP); Universidade Federal de Goiás (UFG) (2013-06-01)Ba(Zr0.75Ti0.25)O3 (BZT-75/25) powders were synthesized by the polymeric precursor method. Samples were structurally characterized by X-ray diffraction (XRD), Rietveld refinement, X-ray absorption near-edge structure (XANES) ...
CRIADO, D.; ZUNIGA, A.; Pereyra, Ines (ELSEVIER SCIENCE BV, 2008)In this work, the structure and morphology of silicon oxynitride films deposited by the PECVD technique were studied. The films were deposited under two different conditions: (a) SiOxNy with chemical compositions varying ...