dc.creatorSantos, Paulo Henrique dos
dc.creatorSinhoreti, Mário Alexandre Coelho
dc.creatorConsani, Simonides
dc.creatorSobrinho, Lourenço Correr
dc.creatorAdabo, Gelson Luis
dc.creatorVaz, Luis Geraldo
dc.date2014-05-27T11:21:23Z
dc.date2016-10-25T18:20:58Z
dc.date2014-05-27T11:21:23Z
dc.date2016-10-25T18:20:58Z
dc.date2005-07-25
dc.date.accessioned2017-04-06T01:14:06Z
dc.date.available2017-04-06T01:14:06Z
dc.identifierJournal of Adhesive Dentistry, v. 7, n. 2, p. 127-131, 2005.
dc.identifier1461-5185
dc.identifierhttp://hdl.handle.net/11449/68344
dc.identifierhttp://acervodigital.unesp.br/handle/11449/68344
dc.identifier10.3290/j.jad.a10284
dc.identifierWOS:000230094300005
dc.identifier2-s2.0-22144491564
dc.identifierhttp://dx.doi.org/10.3290/j.jad.a10284
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/889693
dc.descriptionPurpose: The objective of this study was to verify the effect of cyclic compressive loading on the shear bond strength of an adhesive system following collagen removal. Materials and Methods: Sixty bovine teeth were divided into 4 groups based on the adhesive procedure used: groups 1 and 2 - etching with 35% phosphoric acid and application of the Single Bond adhesive system; groups 3 and 4 - after etching, a 10% sodium hypochlorite solution was applied for 1 min before the application of the adhesive. In all the specimens, a Z100 resin cylinder was built up over the bond area. Groups 2 and 4 were submitted to 500,000 cycles with a load of 100 N. Results: The mean values for the shear bond test (MPa) were: group 1: 7.37 ± 1.15; group 2: 5.72 ± 1.66; group 3: 5.95 ± 1.21; group 4: 3.66 ± 1.12. There was no difference between groups 1 and 2 (p > 0.01). Between groups 1 and 3, 2 and 4, and 3 and 4 there was a significant difference (p < 0.01). The majority of the specimens demonstrated an adhesive failure. Conclusion: The application of sodium hypochlorite on dentin decreased the values of shear bond strength, as did the load cycling in the group treated with sodium hypochlorite.
dc.languageeng
dc.relationJournal of Adhesive Dentistry
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.subjectAdhesive system
dc.subjectBond strength
dc.subjectCollagen removal
dc.subjectSodium hypochlorite
dc.subjectbisphenol A bis(2 hydroxypropyl) ether dimethacrylate
dc.subjectcollagen
dc.subjectdentin bonding agent
dc.subjecthypochlorite sodium
dc.subjectoxidizing agent
dc.subjectphosphoric acid
dc.subjectresin
dc.subjectsilicon dioxide
dc.subjectsingle bond
dc.subjectZ100 composite resin
dc.subjectzirconium
dc.subjectanimal
dc.subjectcattle
dc.subjectchemistry
dc.subjectdental acid etching
dc.subjectdental bonding
dc.subjectdentin
dc.subjectmechanical stress
dc.subjectshear strength
dc.subjectultrastructure
dc.subjectAcid Etching, Dental
dc.subjectBisphenol A-Glycidyl Methacrylate
dc.subjectPhosphoric Acids
dc.subjectShear Strength
dc.subjectSilicon Dioxide
dc.subjectSodium Hypochlorite
dc.subjectStress, Mechanical
dc.subjectZirconium
dc.titleEffect of cyclic compressive loading on the bond strength of an adhesive system to dentin after collagen removal
dc.typeOtro