Analyses of fatigue data in 4340 high strength steel after cadmium electroplating

dc.contributorUniversidade Estadual Paulista (UNESP)
dc.creatorPeres, M. P.
dc.creatorSouza, R. C.
dc.creatorPigatin, W. L.
dc.creatorVoorwald, HJC
dc.creatorMarquis, G.
dc.creatorSolin, J.
dc.date2014-05-20T15:21:32Z
dc.date2016-10-25T17:54:59Z
dc.date2014-05-20T15:21:32Z
dc.date2016-10-25T17:54:59Z
dc.date1998-01-01
dc.date.accessioned2017-04-05T23:31:52Z
dc.date.available2017-04-05T23:31:52Z
dc.identifierFatigue Design 1998, Vol I. Espoo: Technical Research Centre Finland, v. 181, p. 343-349, 1998.
dc.identifier0357-9387
dc.identifierhttp://hdl.handle.net/11449/32658
dc.identifierhttp://acervodigital.unesp.br/handle/11449/32658
dc.identifierWOS:000075029800029
dc.identifierhttp://getinfo.de/app/A-New-12kW-Three-Phase-18-Pulse-High-Power-Factor/id/BLCP%3ACN032174214
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/876950
dc.descriptionBending fatigue tests were carried out to clarify the effects of heat treatment parameters: temperature and time after cadmium electroplating on a high strength steel, to avoid hydrogen embrittlement. Temperatures heat of 190 degrees C, 230 degrees C, 250 degrees C and 300 degrees C at 3, 8 and 24 hours together with the base material electroplated, with and without heat treatment, resulted in 14 conditions studied with respect to fatigue behaviour. Statistical data analysis was performed to identify the best combination temperature/time regarding fatigue strength of the ABNT 4340 steel and the results obtained revealed that the fatigue strength depend on temperature/time conditions.
dc.languageeng
dc.publisherTechnical Research Centre Finland
dc.relationFatigue Design 1998, Vol I
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.subject4340 steel
dc.subjectcadmium electroplating
dc.subjectbending fatigue tests
dc.subjectheat treatment
dc.titleAnalyses of fatigue data in 4340 high strength steel after cadmium electroplating
dc.typeOtro