Genotoxicity and cytotoxicity of mineral trioxide aggregate and regular and white Portland cements on Chinese hamster ovary (CHO) cells in vitro
Registro en:
Oral Surgery Oral Medicine Oral Pathology Oral Radiology and Endodontics. St Louis: Mosby, Inc., v. 101, n. 2, p. 260-263, 2006.
1079-2104
10.1016/j.tripleo.2005.02.080
WOS:000235299200020
0000-0001-5389-0105
Autor
Ribeiro, D. A.
Sugui, M. M.
Matsumoto, M. A.
Duarte, MAH
Marques, MEA
Salvadori, Daisy Maria Favero
Resumen
Objective. Recently, mineral trioxide aggregate (MTA) and Portland cement have been used in dentistry as root-end-filling materials. However, the reported results concerning the biocompatibility of these materials are inconsistent. The goal of this study was to examine the genotoxicity and cytotoxicity of MTA and Portland cements in vitro by the single-cell gel (comet) assay and trypan blue exclusion test.Study design. Chinese hamster ovary (CHO) cells were exposed to MTA and regular and white Portland cements at final concentration ranging from 1 to 1000 mu g/mL for 1 h at 37 degrees C.Results. All compounds tested did not show genotoxic effects in all concentrations evaluated. No significant differences (P > .05) in cytotoxicity were observed for all compounds tested.Conclusions. Taken together, our results suggest that MTA and Portland cements are not genotoxins and are not able to induce cellular death.