Estudo da decomposição térmica de oxalato de estrôncio dopado com cério(III) como precursor de materiais luminescentes

dc.contributorUniversidade Estadual Paulista (UNESP)
dc.creatorFerrari, Jefferson Luis
dc.creatorPires, Ana Maria
dc.creatorDavolos, Marian Rosaly
dc.creatorRibeiro, Clovis Augusto
dc.date2014-05-20T14:19:41Z
dc.date2016-10-25T17:41:13Z
dc.date2014-05-20T14:19:41Z
dc.date2016-10-25T17:41:13Z
dc.date2002-01-01
dc.date.accessioned2017-04-05T22:32:07Z
dc.date.available2017-04-05T22:32:07Z
dc.identifierEclética Química. Fundação Editora da Universidade Estadual Paulista Júlio de Mesquita Filho - UNESP, v. 27, n. spe, p. 315-328, 2002.
dc.identifier0100-4670
dc.identifierhttp://hdl.handle.net/11449/25932
dc.identifierhttp://acervodigital.unesp.br/handle/11449/25932
dc.identifier10.1590/S0100-46702002000200027
dc.identifierS0100-46702002000200027
dc.identifier0000-0002-7984-5908
dc.identifierhttp://dx.doi.org/10.1590/S0100-46702002000200027
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/870763
dc.descriptionEste trabalho trata da obtenção de SrC2O4, Ce2(C2O4)3, e SrC2O4 dopado com diferentes porcentagens de Ce3+ como precursores do luminóforo azul Sr2CeO4. Os precursores preparados foram estudados por TG e DTA. Uma mistura contendo SrC2O4 e Ce2(C2O4)3 na relação 4:1 respectivamente e SrC2O4 dopado com diferentes porcentagens de Ce3+, foram tratadas termicamente à 1100ºC, 12 horas. Os produtos foram analisados por XRD e espectroscopia de luminescência e apresentam mistura das fases SrCeO3, Sr2CeO4 e SrCO3. Os produtos contendo a fase Sr2CeO4 apresentam luminescência azul de banda larga, com exceção daquele obtido a partir de SrC2O4 dopado com 50% de Ce3+. Neste caso a fase predominante é SrCeO3. Pela curva DTA observa-se um pico endotérmico em torno de 1000ºC para todas as amostras, com exceção da amostra dopada em 50%, evidenciando a temperatura de formação da fase Sr2CeO4. A fase luminescente Sr2CeO4 é preferencialmente obtida partindo-se de SrC2O4:Ce3+ 25% e de misturas mecânicas na proporção de 4:1 de oxalatos de estrôncio e de oxalato de cério.
dc.descriptionThis work reports on the preparation of SrC2O4, Ce2(C2O4)3, and SrC2O4 doped with different percentages of Ce3+, as precursors for the new blue phosphor Sr2CeO4. Precursors were studied by using TG and DTA curves. A mixture containing SrC2O4 and Ce2(C2O4)3, in 4:1 ratio as well as SrC2O4 doped with different percentages of Ce3+, were heated under 1100ºC, 12 hours and the resulting products were analyzed by XRD and luminescence spectroscopy. All products prepared under 1100ºC, 12 hours were identified as a mixture of SrCeO3, Sr2CeO4 and SrCO3 phases. All products which Sr2CeO4 phase is detected, present blue wide band luminescence, except the one from SrC2O4 doped with 50% of Ce3+. In this case, the majority phase is SrCeO3 one. All samples DTA curves present endothermic peak ca 1000°C except the 50% doped one indicating the Sr2CeO4 phase formation. Therefore, the blue phosphor Sr2CeO4 is better prepared from SrC2O4:Ce3+ 25% or from SrC2O4 and Ce2(C2O4)3 mixtures.
dc.descriptionFundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
dc.descriptionConselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
dc.languagepor
dc.publisherEditora Unesp
dc.relationEclética Química
dc.rightsinfo:eu-repo/semantics/openAccess
dc.subjectluminescência
dc.subjectanálise térmica
dc.subjectSrC2O4:Ce
dc.subjectSr2CeO4
dc.subjectluminescence
dc.subjectthermal analysis
dc.subjectSrC2O4:Ce
dc.subjectSr2CeO4
dc.titleEstudo da decomposição térmica de oxalato de estrôncio dopado com cério(III) como precursor de materiais luminescentes