| dc.contributor | Bierhalz, Andrea Cristiane Krause | |
| dc.contributor | Universidade Federal de Santa Catarina. | |
| dc.creator | Silva, Lucas Souza da | |
| dc.date | 2023-03-07T13:59:28Z | |
| dc.date | 2023-03-07T13:59:28Z | |
| dc.date | 2022-12-19 | |
| dc.date.accessioned | 2023-09-02T07:02:17Z | |
| dc.date.available | 2023-09-02T07:02:17Z | |
| dc.identifier | https://repositorio.ufsc.br/handle/123456789/244937 | |
| dc.identifier.uri | https://repositorioslatinoamericanos.uchile.cl/handle/2250/8581564 | |
| dc.description | TCC (graduação) - Universidade Federal de Santa Catarina, Campus Blumenau, Engenharia Têxtil. | |
| dc.description | Fios de sutura são responsáveis por aproximar ou unir tecidos, auxiliando na
cicatrização de feridas. Estes podem ser classificados em absorvíveis, que são
degradados pelo organismo, ou não absorvíveis, que devem ser retirados após a
cicatrização. Os fios de sutura absorvíveis são de grande interesse para diversas
aplicações médicas, porém, existem poucas opções de materiais alternativos ao fio
de origem animal, que apresentem elevada biocompatibilidade e provoquem baixa
reação tecidual. Deste modo, o uso de polímeros naturais como o alginato e a
quitosana, para o desenvolvimento de fios de sutura tem despertado grande
interesse, pois além de serem absorvíveis estes materiais são biocompatíveis e
possuem baixa toxicidade. Todavia, suas características mecânicas precisam ser
melhoradas para possibilitá-las a esta aplicação. Este estudo teve como objetivo
desenvolver filamentos de alginato, por meio da técnica de fiação a úmido, utilizando
concentrações poliméricas de 2 e 2,5 % (m/v) e banhos de coagulação contendo
cloreto de cálcio (CaCl2) em concentrações de 7,5 e 10 % (m/v). Os filamentos
obtidos passaram por um revestimento posterior ao processo de fiação, utilizando
uma solução de quitosana em concentração de 2,5 % (m/v), com adição de ZnO em
concentração de 0,1 % (m/v). Caracterizações foram feitas com relação a
densidade linear, absorção e perda de massa em água e resistência à tração. Com o
objetivo de formar filamentos ativos, o fármaco anti-inflamatório diclofenaco de sódio
foi incorporado na matriz de alginato ou no recobrimento de quitosana e a liberação
in vitro em água a 37°C foi avaliada. Os resultados apontaram um aumento na
densidade linear com o aumento da concentração de alginato e cloreto de cálcio. O
revestimento de quitosana aparentou ter formado um complexo polieletrólito em
associação com o alginato, sendo que sua adição melhorou características de
tensão a ruptura, módulo de elasticidade e reduziu a ductilidade do material. A
quitosana trouxe ao filamento maior capacidade de absorção e uma perda de massa
reduzida. Os testes de liberação in vitro indicaram uma liberação mais lenta e
prolongada e em maior quantidade quando o fármaco é inserido na matriz de
alginato. Além de suas já conhecidas utilidades na área médica, filamentos de
alginato de cálcio demonstram potencial aplicabilidade como fio de sutura, visto que
a reticulação com íons cálcio permite modificar propriedades. Adicionalmente, o
revestimento de quitosana associado a processos de estiramento pode melhorar as
características mecânicas e contribuir com o desenvolvimento de um material com
liberação prolongada de agentes terapêuticos. | |
| dc.description | Surgical sutures are responsible for closing wounds and aiding in healing. These can
be classified as absorbable, which are degraded by the body, or non-absorbable,
which must be removed after healing. Absorbable suture threads are of great interest
for various medical applications, however, there are few options for alternative
materials to animal thread which have high biocompatibility and cause low tissue
reaction. Therefore, the use of natural polymers such as alginate and chitosan for the
development of surgical suture has aroused great interest, because in addition to
being absorbable, these materials are biocompatible and have low toxicity. However,
their mechanical properties need to be improved to enable them for this application.
This study aimed to develop alginate filaments, through the wet spinning technique,
using polymeric concentrations of 2 and 2.5% (w/v) and coagulation baths containing
calcium chloride (CaCl2) in concentrations of 7, 5 and 10% (m/v). The filaments
obtained underwent a coating after the spinning process, using a chitosan solution at
a concentration of 2.5% (w/v), with the addition of ZnO at a concentration of 0.1%
(w/v). Characterizations were made with respect to the linear density, absorption and
weight loss in water and tensile strength. With the aim of forming active filaments, the
anti-inflammatory drug diclofenac sodium was incorporated into the alginate matrix or
into the chitosan coating and the in vitro release in water at 37°C was evaluated. The
results showed an increase in the linear density with the increase in the
concentration of alginate and calcium chloride. The chitosan coating appeared to
have formed a polyelectrolyte complex in association with the alginate, and its
addition improved stress-at-rupture characteristics, modulus of elasticity, and reduced
the ductility of the material. Chitosan brought greater absorption capacity to the
filament and reduced mass loss. The in vitro release tests indicated a slower and
more prolonged release and in greater amount when the drug is inserted into the
alginate matrix. In addition to their well-known uses in the medical field, calcium
alginate filaments demonstrate potential applicability as a surgical suture, since
crosslinking with calcium ions allows for the modification of properties. In addition,
the chitosan coating associated with stretching processes can improve the
mechanical characteristics and contribute to the development of a material with
prolonged release of therapeutic agents. | |
| dc.format | 64 f. | |
| dc.format | application/pdf | |
| dc.language | pt_BR | |
| dc.publisher | Blumenau, SC. | |
| dc.rights | Open Access. | |
| dc.subject | Fio de sutura | |
| dc.subject | Alginato | |
| dc.subject | Quitosana | |
| dc.subject | Têxteis médicos | |
| dc.subject | Surgical Suture | |
| dc.subject | Alginate | |
| dc.subject | Chitosan | |
| dc.subject | Medtech | |
| dc.title | Obtenção de filamentos de alginato de cálcio com revestimento de quitosana para aplicações biomédicas | |
| dc.type | TCCgrad | |