Influência do HEMA em sistemas adesivos universais contendo 10-mdp, nas propriedades adesivas imediatas

dc.contributorLoguercio, Alessandro Dourado
dc.contributor381.969.132-49
dc.contributorhttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4763905J5&tokenCaptchar=03AKH6MRHX9KwXsxjhjvSBFM7FL_La3lesoWHPBvF6gDU30hWZPygcp_Vy3-8ACAs3D0nm5KBU4U4nQW8yi4wMbF0NX6DnSBRw7Pj5A0iMODOEhM8PT_hCLxjTAPuVs1YPeObnC-2kCnFLvVF6MP6CQJkJ_HNxfm7jiMLZ-NHi-jEGa0NOTle2knf-NB0gvFI0uxCNKbPiLvGPAj0GGbPdmaQAHjQ2B_rX0x547aQ_gOSO9m6ION8ctB5dhiRTA9_wtGgORuKtu2ZxFhrymvcSm3vR6ph9m4IIlfx5UCl_exLV60kWV1W4Y0ygmK-b51kRHE7XobRrj24cuqSAg19eSAnOyV0ndVrXuhfTMaThcSAtKNeQEaCSS-6OqSBV2YMwbdBkKBpqSZgv5j-1Z5QlkdsNHXUtzPBwsl_tPGRn3t7MQ2iOEVNkMFza_H1EAGcB2apTRGJrb43A_vWlePAUclDhMVdcN6zycyvLbyQzBCrbpAUUhkKIdIiLrvqJCuZKS3ZPRN4YSzS1kuOG5dqFPQyRUxdbOTfYmQ
dc.contributorCardenas, Andres Felipe Millan
dc.contributor012.200.409-40
dc.contributorhttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4373908J9&tokenCaptchar=03AKH6MRG7Vg3S0pjZ4GarqkBl9WzLuIj1YraJ77Zbm0V00soHnckO_-faqE7c01lv4AZ0F-S4cqGEFFx8U2QgKldDyFihS7CnCdswPJBdKJEGHjSIto4OvYhvREg-W1vQDvVMUmJDhR158TP1mnc2MtupvF5IOaPyQNvSSMHwEHU9Mdka5VKyqb4l0WGyO6DivV4TnlxKoSAyhLWXEoh7-A3T7wsKqJI58j1CJ-vbIsHg-2KWJgyPPREP1hBtYfIlRMVuEDHH8PbRk4jaMLDdehi2GW8Vn5KY8cXaW0xr8ybHOlbcZhKVmoBznWJ2glhYdeP8qOJky0fFWuQwsk9qCV3R57Vzdo0ZSzow74eG0foJm0WIOwfsOvwLeJmjkckNDBk08CgZrAsgvFEytIYp-wRDs5A_K60I7ZMm4fdo25SeFtZpjm903-1ZT0YeGP6V_ptR3R-Qnw7GJU9u7786wZpz7j6vErR7sPtGV_xuYI0ySM5E1LETgy1IrNVkP-rwNk7tQqko77JiT28pXpzax3PMVgq-YPPlkg
dc.contributorMoraes, Rafael Ratto de
dc.contributor000.928.880-54
dc.contributorhttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4732086Z6&tokenCaptchar=03AKH6MREIh0FbbN39ARHJfyf_ciLkb-6rkcSEChg12tyrDJYpt5-5kAJsYp3dbGYZY9iyWwkeLS1fsOoxQRo08b0-U2OV6hSTuljCVLchGVj8RmOVbm2pNg1DzNjEkxj6xbRNJg5YsjYXl0Z9PpaMxss_g85EaegzxWOrH4QaZqPWoD4RRWtR6BwT_1cq1yt7IAQTc2NWdkwWXSJK0BgkdbZTU5BdjIlKoNK8j4QYF4mFvWyF3VQp85YvMfAiiEAFTlxXVd6xX_QBC8CMywu8F3mN3ulqDNN-CJ5k3O8sY7C5mppmDmYjqau3-GJFsg15QN_oip5iYG3BdGWn0ZwZ1MQabMakZe4LIv_i91wBofSRGifucEAvri1Ori7irz1TqStdPjpVxNCKJcBEF2yxSK6DzVI2_nobSvy8U2nHiADlNoNiPHdRMJ64HSCHX-wkN9CecCnbcX8q4QmRqLUM62VNrUYttat7A737fC6HEU9Qa_rjo26OXGt87e9IdiDET4Ss4SfUqUiTVNJoG1N2oZQFhAmZHRIGsA
dc.contributorGutierrez, Mario Felipe
dc.contributor012.970.359-17
dc.contributorhttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4432402U3&tokenCaptchar=03AKH6MRFMl3Z9W81TqFStNpvUtQxuVjJ08ASuLZx67hMX9o6NcyFk64bVh7GgfHyFeWxCRoA7fWHbWlgbqqW_MdsNVkMJ5m2Wg7DWQMGphp1jdWdDEoO1xDYIW9e9U8BHuh4tflCIjMme6zCh8RTSSZEUnlzGTUOXBikzPyfeyuTWvbUvv4SkwNA1PT03VHiqIC5jwq8LFHfofmXnTzY2MsHwM3-BqeFX-yMGZHFPL0Plpc3Bunx_XLZR4xHXxvQfW_AXbd9xF7U-KRNNZKU9BWFcLJ0wbpg1MMdUx38Hy3ppjSoUb76cZmBb9SkNsNFEtwFZrgaPxkGwCRdWI3XXZ2rTpCTJeR0OvlR5era1Hq69wOB0QNm6rrlBkhxanynPmN81gA9Xi2H77EOHEYQ8J0b2kx248s94SuTNaVXky47-QLCzxcCUI3fjOMx3dIYYCotgVTYIixo2u9j8iV6PjVv6s2J2_b6NlynpPanQIhDwN2BgVCKkHa0C5d0XvXn8GhLVVR8fRFGPojIE-WUqlRPtBBLvZrgKKw
dc.contributorUniversidade Federal de Pelotas (UFPEL)
dc.contributorUniversidad de los Andes
dc.contributorUniversidade Ceuma
dc.creatorFerreira, Michel Wendlinger Cantanhede
dc.date2023-04-12T21:56:26Z
dc.date2023-04-12
dc.date2023-04-12T21:56:26Z
dc.date2022-02-16
dc.date.accessioned2023-08-31T23:35:55Z
dc.date.available2023-08-31T23:35:55Z
dc.identifierFERREIRA, Michel Wendlinger Cantanhede. Influência do HEMA em sistemas adesivos universais contendo 10-MDP nas propriedades adesivas imediatas. 2022. Dissertação (Mestrado em Odontologia) - Universidade Estadual de Ponta Grossa, Ponta Grossa, 2023.
dc.identifierhttp://tede2.uepg.br/jspui/handle/prefix/3874
dc.identifier.urihttps://repositorioslatinoamericanos.uchile.cl/handle/2250/8568747
dc.descriptionPurpose: to evaluated the effect of the presence of HEMA in universal adhesives systems with 10-MDP on the immediate adhesive properties to enamel and dentin. Material and methods: One hundred and twelve caries-free third molars were divided to be tested for dentin (n=72) and for enamel (n=48) tests. For each substrate, teeth were divided into 8 experimental groups according to the following: Adhesives: 1) Scotchbond Universal (SBU, 3M Oral Care, USA); 2) Gluma Bond Universal (GBU, Kulzer, Germany); 3) Solare Universal Bond (SUB, GC, America); 4) Zipbond Universal (ZIP, SDI, Australia) and Adhesive Strategy: Etch-and-rinse (ER) and Self-etch (SE) mode. For dentin tests, the occlusal third of the crown of all teeth was removed, and the adhesive protocol was applied. After completing restoration, specimens were sectioned into bonded sticks (0.8 mm2 ) and tested by microtensile bond strength (μTBS), in situ degree of conversion (DC) and nanoleakage (NL) by scanning electron microscopy. For enamel tests, teeth were sectioned in four parts (buccal, lingual, mesial and distal) and adhesive protocol was applied. After completing restoration, specimens were tested by microshear bond strength (μSBS). For in situ degree of conversion (DC) and nanoleakage (NL) evaluation to enamel, the specimens were sectioned in slices previously to be evaluated. Data of each substrate were subjected to two-way ANOVA and Tukey's test (α = 0.05) for each property evaluated. Results: The adhesives SBU and ZIP showed the highest μTBS, SBS, DC and lower values of NL when compared to GBU and SUB for both strategies (p=0.001). ER strategy presented higher values of μTBS and SBS when compared to SE strategy (p=0.001), with exception for SBU. Conclusion: The effect of the presence or not of HEMA in commercial universal adhesives systems containing 10-MDP on enamel and dentin adhesive properties appears to be material dependent.
dc.descriptionEste estudo avaliou o efeito da presença de HEMA em sistemas adesivos universais contendo 10-MDP, nas propriedades adesivas imediatas ao esmalte e dentina. Material e métodos: Cento e vinte terceiros molares hígidos foram divididos e testados para dentina (n = 72) e para esmalte (n = 48). Para cada substrato, os dentes foram divididos em 8 grupos experimentais de acordo com os seguintes fatores: Adesivos: 1) Scotchbond Universal (SBU, 3M Oral Care, USA); 2) Gluma Bond Universal (GBU, Kulzer, Alemanha); 3) Solare Universal Bond (SUB, GC, América); 4) Zipbond (ZIP, SDI, Australia) e estratégia adesiva: condicionamento e lavagem (CL) e autocondicionante (AC). Para os testes de dentina, o terço oclusal da coroa de todos os dentes foi removido e o protocolo adesivo foi aplicado. Após completar a restauração, os espécimes foram seccionados em palitos da interface adesiva (0,8 mm2) e testados por resistência de união por microtração (μTBS), grau de conversão in situ (GC) e nanoinfiltração (NI). Para os testes de esmalte, os dentes foram seccionados em quatro partes (vestibular, lingual, mesial e distal) e aplicado protocolo adesivo. Após restauração, os espécimes foram testados por resistência de união por microcisalhamento (μSBS). Para avaliação do GC e NI em esmalte, os corpos-de-prova restaurados e seccionados em fatias para realização das análises. Os dados de cada substrato foram submetidos à análise de variância de 2 fatores e teste de Tukey (α = 0,05) para cada propriedade avaliada. Resultados: Os adesivos SBU e ZIP apresentaram maiores μTBS, μSBS, GC e menores valores de NI quando comparados ao GBU e SUB para ambas as estratégias e substratos (p = 0,001). A estratégia CL apresentou maiores valores de μTBS e μSBS quando comparada à estratégia AC (p = 0,001), com exceção do SBU. Conclusão: o efeito da presença ou não de HEMA em sistemas adesivos universais comerciais 10-MDP nas propriedades adesivas de esmalte e dentina parece ser dependente do material.
dc.languagepor
dc.publisherUniversidade Estadual de Ponta Grossa
dc.publisherBrasil
dc.publisherDepartamento de Odontologia
dc.publisherPrograma de Pós-Graduação em Odontologia
dc.publisherUEPG
dc.rightsAcesso Aberto
dc.rightsAttribution-NonCommercial-NoDerivs 3.0 Brazil
dc.rightshttp://creativecommons.org/licenses/by-nc-nd/3.0/br/
dc.subjectAdesivos dentinários
dc.subjectEsmalte dental
dc.subjectDentina
dc.subjectDentin-Bonding Agents
dc.subjectEnamel
dc.subjectDentin
dc.subjectCNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
dc.titleInfluência do HEMA em sistemas adesivos universais contendo 10-mdp, nas propriedades adesivas imediatas
dc.typeDissertação


Este ítem pertenece a la siguiente institución