| dc.contributor | Chinelatto, Adilson Luiz | |
| dc.contributor | 068.695.848-93 | |
| dc.contributor | http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4727364Z3&tokenCaptchar=03ANYolqsM3BEbYQEQHWs1Tm4UddgGBphwT7c74EeXsfnrS_hVmM_Ye3ZAmndxlCUrmtrF-IhPlChSGyDcgAPMQk2eTEpr2UbxDac55WaACJmHbheTZvsuFjeMiWLnZGvYIVkxPVxWY9qT_jig6YvVgVg8rF1BMrOvw_MnvTcrgAKtxwYTBI38eJPZCmfr-9s5vGc-8FiV_BFmCSO9uKMgRL6WYx7imjzysOcKAhC9PwymaBeXNxRTJXnyk4ZW3-5H0L-oabEFWzC56FQ_KSThgH5n24RXl0TPLXqXxflpQkteD_PssoJ01NTtipRwiue4pPAcNn81KQKJFG5ZlzdTxcED6IACXxO3Pzb6useZW7qTRjAoQpkB23YF1Z1pq3yhsM1GLAcIhD2R0jYKCrnLvwlYD1ncUweEvSRDHeMWPYwyUTJimvWqBc7K3n5Sun_y1oaJlPTE8DrZxe4mjHILIPeLY8P3RcKriaLxFr_snMEfExQcAdunaV4xObIkXJ2dxp02t-7S4Z09JgW-nwU2--bKlwb1HqYoSXHWKNq2_HAh_jYSmDaxTZfPJWjbAXeApJKkmsxD9N9IoON6V7sQrsXA73DpRM6OUw | |
| dc.contributor | Ramos, Kethlinn | |
| dc.contributor | 053.186.599-18 | |
| dc.contributor | http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4364135E7&tokenCaptchar=03ANYolquyACMSeg4Yc2zn-g2BRD3ECqlLBxVfhSB5i1MMdc3hFLYhbOPMXg1hYLvZ1a4xeoDPxRUYXD4lcj4DBruw6HLUnrzuDt41jnZcdK9aV1RUpQtXp0Vn_ik0x_cCwCMDziI2hI44dZW0aF93tp5fgqsi6JtrQiWX3owKojkKTwGMcLjFKJu6GexRPb9PmA754J15LgTQ5-KutNGGxPxXt844u8Y-aSgva1pPDeYeuejTjE8_mIvh7zwWkShNlK1DSZbAJ2CCvwdOzzxcaYfv37yDxpkdXiy_dsAG2BGf7R2IlATVTwXs1GYBWMtO_jMOZEwwxlIR2RAR5MdhbgAY_LQ_-hVoPp-sdmVoNCs_deBcRqSJrSaoD8zw40ioOlHjsDHGXjVWoLaowt7eokjs0W72OmzoaShmKrw3On5ZwQhby3jDXUqP6RT42Wlh410m6CbxzknNvwlmNefDwyu-Up604NbAFZ_cJuAE-WKeT-opa9cmhOuwMB69mocMLTo5o4wTEwO67zVwS7verYh6iNZNPCXzMvPiMPe2tNjYmZtyM5ApKW8FTOQ4ZBFoV4rK3vUGEIyFrdq3_PlyoVNIPQIGS7K1kA | |
| dc.contributor | Wendler, Leonardo Pacheco | |
| dc.contributor | 063.497.319 | |
| dc.contributor | http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4298910Z5&tokenCaptchar=03ANYolqv6cHoEpq_yGgxe5fNJBA3RPWqUvVf-prGPy6_WeiGMkmlMyoPAyVKGh0Pjngw-BnuSjPt3vySMlWJTWsIvpQBExwBO4_JUbHRh_ayKv62cfcuVuzuZjfz34EIS9QTWXl8TZz9lyDPj1L2TTYDyGZQHoUpruwEBTm-2A92rDi-R7O2w6Ug3zf5cHx8LTxnZpQrXYNfDtri_nVCIfCu3UosKNJJ9aYIxkvvzeW3HSspqiaw-9cSDmvbxBB-hoZonrOK8WmiuNeqzcthBCTz5UejXJoY47IHg47AQemyE373vEzi1hdZy5MNgNJbURLk6BLPHgVG506krR8Jfp2ZaZ4WU_hbzDtPo4O5x-C0WZqPjpWG7STKSXdUWKPx01cyHj_sGzRRB6k6oCrc888rj104WR_qqfAIBs0DO2w_N5WN9H-dbOQk9PjjrLQE8iAU0v1IfgM7Fa_xAlys8OTJO4_t9rYDo334sRwnJWhExz_FQSOSmSKmiPb3okgg8ss1a2CqVy2za9JI6MTNuCTVY0YPnhy8v5UwX9IWPliXVL1JsyyPvS6gyoXtuAMzSrv7d_O7dvQ6WjlS7aTws9N7ewwbCdPrUBA | |
| dc.contributor | Cerri, José Alberto | |
| dc.contributor | 077.836.538-71 | |
| dc.contributor | http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4784774Z0&tokenCaptchar=03ANYolqvrn1nIver2BI7cIFfuZhow8vf5FonaCcoMAcp1qKfEbq9ajzob2_qXX88U_zUl6ERaRj1LDKMlQvzpv1KJOUyFkH1tzTk91a-eEgavt3G7o6KtgIHcQvVxrc0lXfuZ5yT6QZ1zqXm4TOoRtbk9D21Mo7dnkUC00WlrezzBkwVVpRwrXKO6osKu7RUFi2O_5MI9gyTpzv7MUB3BE2izU80NzvkcRNrFRbL66Mvl8QuogEoCqFkPQbPudP7TcBspw6o59rECC8Gva7IO19xTJ_WXzc-28l-M_WfllorHib8kC5PNGLNkl3xRPYkl9EkVP2RSOwB4spD142F6Nws_lmdizX2rCnylROGt6kiOjO86ExngcuxwtNa9skub1lIGUuOnpZiUlPiupdrEh_Skys-TcrTDNaxGCGP5ovkml0DgjjCnlq-vXXS3kr2Egde9Ckco-5fsxJMvLLqKdMgdwnFccESJVvxbDFjOimH9muJ-s0L39wV7Qf5J1x37FRZVDFdf_p79hBKj8Cwsk8oLHL_UxSNJU8VswvG9ZFr0aOBpecRr8Lr3NZIRN-slMjnNh10WMathuweQQ_YPIpCYSnlyJjiKrg | |
| dc.contributor | Universidade Estadual de Ponta Grossa | |
| dc.contributor | Universidade Tecnológica Federal do Paraná - UTFPR | |
| dc.contributor | Universidade Estadual de Ponta Grossa (UEPG) | |
| dc.creator | Alves, Gustavo Souza | |
| dc.date | 2022-07-21T16:51:31Z | |
| dc.date | 2022-07-21 | |
| dc.date | 2022-07-21T16:51:31Z | |
| dc.date | 2022-02-18 | |
| dc.date.accessioned | 2023-08-31T23:35:25Z | |
| dc.date.available | 2023-08-31T23:35:25Z | |
| dc.identifier | ALVES, Gustavo Souza. Obtenção e caracterização de cermetos Ni-BCZY para uso como ânodo de células a combustível. 2022. Dissertação (Mestrado em Engenharia e Ciências dos Materiais) - Universidade Estadual de Ponta Grossa. 2022. | |
| dc.identifier | http://tede2.uepg.br/jspui/handle/prefix/3674 | |
| dc.identifier.uri | https://repositorioslatinoamericanos.uchile.cl/handle/2250/8568552 | |
| dc.description | The fuel cells are defined as devices with the ability to convert electrochemical energy
into electrical energy and heat, having water as the main by-product. Several types
and variations of fuel cells are studied and already have practical applications,
including solid oxide fuel cells, characterized by the use of ceramic material as
electrolyte. One of the main obstacles for its use is the high temperature, remaining
between 600°C and 1000°C, reducing its useful life and the range of applications. The
progress of the studies led to the use of oxides with proton type conduction, opening
the way to reduce the temperature range for cell use, reaching temperatures between
400°C and 700°C. These cells came to be known as protonic ceramic fuel cells, and it
uses materials with perovskite-like structures. Therefore, there are compounds such
as Ba(Ce, Zr, Y)O3 (BCZY), which has characteristics such as good proton conductivity
and good chemical stability. When used as anodes, nickel-based cermets (Ni) are
widely studied, thus joining this metal with the material used in the electrolyte, such as
BCZY. This work studied the use of Ni-BCZY cermet for use in protonic ceramic fuel
cell anodes. The BCZY, with Ba(Ce0,2Zr0,7Y0,1)O3-δ composition, was obtained through
synthesis based on the Pechini method. The formation of cermet was performed by a
mechanical mixture in eccentric vibrating mill, between NiO and BCZY, in weight ratios
of 40/60, 50/50 and 60/40 respectively. The electrical properties were evaluated by
impedance spectroscopy, after heat treatment to reduce NiO to Ni. The cermets was
observed in the three proportions studied, with characteristics such as the percentage
of porosity and electrical conductivity suitable for each proportion. The compositions
Ni-BCZY 60/40 and Ni-BCZY 50/50 showed conductivity values above 0.1 S/cm and
activation energies of 0.02 eV/atom, demonstrating the feasibility of using as anode.
With the results presented, the Ni-BCZY 50/50 composition was used to form a
symmetric cell, it having BCY as an electrolyte, thus verifying the formation of this
configuration and the electrical behavior of this type of cell. | |
| dc.description | As células a combustível são definidas como dispositivos com a capacidade de
converter energia eletroquímica em energia elétrica e calor, tendo como principal
subproduto a água. Diversos tipos e variações de células a combustível são estudadas
e já apresentam aplicações práticas, entre estas pode-se encontrar as células a
combustível de óxido sólido, caracterizadas pela utilização de material cerâmico como
eletrólito. Um dos principais entraves para a utilização é a elevada temperatura de
operação, na faixa entre 600°C e 1000°C, reduzindo a vida útil e a gama de
aplicações. O avanço dos estudos levou à utilização de óxidos com condução do tipo
protônica, abrindo caminho para redução da faixa de temperatura de utilização das
células, atingindo temperaturas entre 400°C a 700°C. Estas células passaram a ser
conhecidas como células a combustível de óxido sólido com condutividade protônica,
e utilizam materiais com estruturas tipo perovskitas. Entre essas, encontram-se
compostos como o Ba(Ce, Zr, Y)O3 (BCZY), o qual apresenta características como
boa condutividade protônica e boa estabilidade química. Na utilização como ânodos,
cermetos baseados em níquel (Ni) são muito estudados, juntando assim este metal
com o material utilizado no eletrólito, como o próprio BCZY. Desta forma, esse trabalho
estudou a utilização do cermeto Ni-BCZY para a uso em ânodos de células a
combustível de óxido sólido com condutividade protônica. O BCZY com composição
Ba(Ce0,2Zr0,7Y0,1)O3-δ foi obtido por meio de síntese baseada no método Pechini. A
formação do cermeto foi realizada a partir de mistura mecânica por moagem em
moinho excêntrico, entre NiO e BCZY, em relações de massa de 60/40, 50/50 e 40/60,
respectivamente. As propriedades elétricas foram avaliadas por espectroscopia de
impedância, após tratamento térmico para redução do NiO em Ni. Constatou-se a
formação do cermeto nas três proporções estudadas, tendo características como a
porcentagem de porosidade e condutividade elétrica adequadas para cada proporção.
Dentre as composições, as Ni-BCZY 60/40 e Ni-BCZY 50/50 apresentaram valores de
condutividade acima de 0,1 S/cm e energias de ativação de 0,02 eV/átomo,
demonstrando a viabilidade na utilização como ânodo. Com os resultados
apresentados, a composição Ni-BCZY 50/50 foi utilizada para formação de uma célula
simétrica, tendo o BCY como eletrólito, verificando assim a formação dessa
configuração e o comportamento elétrico desse tipo de célula. | |
| dc.description | Coordenação de Aperfeiçoamento de Pessoal de Nível Superior | |
| dc.language | por | |
| dc.publisher | Universidade Estadual de Ponta Grossa | |
| dc.publisher | Brasil | |
| dc.publisher | Departamento de Engenharia de Materiais | |
| dc.publisher | Programa de Pós-Graduação em Engenharia e Ciências de Materiais | |
| dc.publisher | UEPG | |
| dc.rights | Acesso Aberto | |
| dc.rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil | |
| dc.rights | http://creativecommons.org/licenses/by-nc-nd/3.0/br/ | |
| dc.subject | Cermeto | |
| dc.subject | Ni-BCZY | |
| dc.subject | ânodo | |
| dc.subject | células a combustível | |
| dc.subject | Cermet | |
| dc.subject | Ni-BCZY | |
| dc.subject | anode | |
| dc.subject | fuel cell | |
| dc.subject | CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA | |
| dc.title | Obtenção e caracterização de cermetos Ni-BCZY para uso como ânodo de células a combustível. | |
| dc.type | Dissertação | |