Transformaciones microestructurales de uniones soldadas de acero inoxidable austenítico con acero inoxidable ferrítico

dc.creatorTabares, Ramón
dc.creatorSerna Giraldo, Claudia Patricia
dc.date2017-01-07T14:55:42Z
dc.date2017-01-07T14:55:42Z
dc.date2014
dc.date.accessioned2023-08-28T20:45:05Z
dc.date.available2023-08-28T20:45:05Z
dc.identifierS. Aguilar , R. Tabares and C. Serna , “Transformaciones microestructurales de uniones soldadas de acero inoxidable austenítico con acero inoxidable ferrítico”, Revista Colombiana de Materiales, no. 5, pp. 1-6, 2014.
dc.identifier2256-1013
dc.identifierhttp://hdl.handle.net/10495/5793
dc.identifier.urihttps://repositorioslatinoamericanos.uchile.cl/handle/2250/8483751
dc.descriptionRESUMEN: En este trabajo se estudian los fenómenos metalúrgicos que ocurren en la soldadura SMAW de un acero inoxidable ferrítico AISI 430 con un acero inoxidable austenítico AISI 316L. Para el estudio se utilizaron dos tipos de electrodos: austenítico AWS E309L y dúplex AWS E2209-16, ambos con un diámetro de 3.2 mm. La unión se realizó con un solo pase y manteniendo alta la entrada de calor. Se evaluó la influencia del tipo de electrodo en la evolución microestructural de la zona afectada por el calor y de la zona de fusión, encontrando diferencias en la morfología de la ferrita δ para ambos depósitos, evidenciando crecimiento y refinación de grano ferrítico y formación de martensita en la zona afectada por el calor del metal base ferrítico. Se evaluó también la resistencia a la tensión hallando similitudes en los dos depósitos. La dureza y el porcentaje de ferrita δ fueron medidos.
dc.descriptionABSTRACT: The metallurgical transformations of SMAW welding of AISI 316L austenitic stainless steel with AISI 430 ferritic stainless steel were studied. Two different electrodes, AWS E309L austenitic and AWS E2209-16 duplex stainless steels 3.2 mm diameter were used to perform the study. The joining was made with a single pass welding and keeping a high heat input. The influence that the electrodes have on the microstructural evolution in the heat affected zone and fusion zone was evaluated. Differences between δ ferrite morphology were found for both weld metals. The heat affected zone of the ferritic side showed grain coarsening and grain refinement with martensite at the grain boundaries. Tensile strength was similar for both welding conditions. Microhardness and δ ferrite percentage were measured as well.
dc.format5
dc.formatapplication/pdf
dc.formatapplication/pdf
dc.languagespa
dc.publisherUniversidad de Antioquia, Facultad de Ingeniería
dc.publisherInvestigaciones Pirometalúrgicas y de Materiales (GIPIMME)
dc.publisherMedellín, Colombia
dc.rightsAtribución-NoComercial-CompartirIgual 2.5 Colombia (CC BY-NC-SA 2.5 CO)
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rightshttps://creativecommons.org/licenses/by-nc-sa/2.5/co/
dc.rightshttp://purl.org/coar/access_right/c_abf2
dc.rightshttps://creativecommons.org/licenses/by-nc-sa/4.0/
dc.subjectUniones soldadas
dc.subjectAcero inoxidable austenítico
dc.subjectAcero inoxidable ferrítico
dc.subjectSoldadura de aceros inoxidables
dc.subjectSMAW
dc.subjectMetalurgia de la soldadura
dc.titleTransformaciones microestructurales de uniones soldadas de acero inoxidable austenítico con acero inoxidable ferrítico
dc.typeinfo:eu-repo/semantics/article
dc.typeinfo:eu-repo/semantics/publishedVersion
dc.typehttp://purl.org/coar/resource_type/c_2df8fbb1
dc.typehttps://purl.org/redcol/resource_type/ART
dc.typeArtículo de investigación


Este ítem pertenece a la siguiente institución