Evaluación del comportamiento in vitro de recubrimientos de hidroxiapatita depositados mediante proyección térmica por combustión oxiacetilénica sobre un sustrato de Ti6AI4V

In vitro evaluation of oxy-fuel thermal sprayed hydroxyapatite coatings onto Ti6AI4V substrates

dc.creatorCopete López, Hamilton
dc.creatorLópez Gómez, María Esperanza
dc.creatorVargas Galvis, Fabio
dc.creatorEchavarría Velásquez, Alejandro Iván
dc.creatorRíos, Tatiana
dc.date2021-10-21T21:43:07Z
dc.date2021-10-21T21:43:07Z
dc.date2013
dc.date.accessioned2023-08-28T20:07:39Z
dc.date.available2023-08-28T20:07:39Z
dc.identifier0012-7353
dc.identifierhttp://hdl.handle.net/10495/23362
dc.identifier2346-2183
dc.identifier.urihttps://repositorioslatinoamericanos.uchile.cl/handle/2250/8474273
dc.descriptionRESUMEN: Recubrimientos de Hidroxiapatita sintética producida por precipitación y calcinación a 850 °C fueron depositados sobre sustratos de Ti6Al4V mediante proyección térmica por combustión. Las fases presentes en el material sintetizado y en los recubrimientos elaborados fueron determinadas mediante Difracción de Rayos X. Los recubrimientos fueron evaluados en condiciones in vitro con fluido fisiológico a 37 °C que simula el plasma humano, por periodos de 3, 7, 15 y 30 días. La superficie de los recubrimientos fue caracterizada antes y después de los ensayos in vitro mediante Microscopía Electrónica de Barrido y por Barrido de Energía Dispersiva. La concentración de iones de fosfato y de calcio en el fluido fisiológico fue determinada mediante espectrofotometría. Los resultados de las pruebas in vitro sugieren la acción de dos mecanismos: disolución del recubrimiento en el fluido fisiológico y posterior precipitación de cristales de calcio y fósforo sobre la superficie de la capa de Hidroxiapatita
dc.descriptionABSTRACT: Coatings were elaborated onto Ti6Al4V substrates using the oxyacetylene flame spraying process from hydroxyapatite synthesized by precipitation and calcination to 850 °C. The phases in the hydroxyapatite powders and coatings were determined by X Ray Diffraction. The surface of coating was exposed to in vitro condition using a Simulated Biological Fluid (SBF), which was heated to 37 °C. The in vitro tests were realized during 3, 7, 15 and 30 days. The surface of coatings was evaluated before and after the in vitro tests, by Scanning Electron Microscopy and chemical microanalysis was realized by Energy Dispersive X-Ray Spectroscopy, while the phosphate and calcium ions in the SBF were determined by spectrophotometry. The in vitro tests results indicate that phosphate and calcium ions were dissolved from the surface of coating to fluid and then, calcium phosphate crystals were precipitate on the coatings
dc.descriptionCOL0012659
dc.descriptionCOL0083393
dc.format8
dc.formatapplication/pdf
dc.formatapplication/pdf
dc.languagespa
dc.publisherUniversidad Nacional de Colombia, Facultad de Minas, Centro de Publicaciones
dc.publisherGIMACYR - Grupo de Investigación en Materiales y Recubrimientos Cerámicos
dc.publisherInvestigaciones Pirometalúrgicas y de Materiales (GIPIMME)
dc.publisherMedellín, Colombia
dc.relationDyna
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rightshttp://creativecommons.org/licenses/by-nc-nd/2.5/co/
dc.rightshttp://purl.org/coar/access_right/c_abf2
dc.rightshttps://creativecommons.org/licenses/by-nc-nd/4.0/
dc.subjectTécnicas In Vitro
dc.subjectIn Vitro Techniques
dc.subjectMateriales Biocompatibles
dc.subjectBiocompatible Materials
dc.subjectCombustión
dc.subjectCombustion
dc.subjectHidroxiapatitas
dc.subjectRecubrimiento
dc.subjectProyección térmica
dc.subjectHidroxiapatitas
dc.titleEvaluación del comportamiento in vitro de recubrimientos de hidroxiapatita depositados mediante proyección térmica por combustión oxiacetilénica sobre un sustrato de Ti6AI4V
dc.titleIn vitro evaluation of oxy-fuel thermal sprayed hydroxyapatite coatings onto Ti6AI4V substrates
dc.typeinfo:eu-repo/semantics/article
dc.typeinfo:eu-repo/semantics/publishedVersion
dc.typehttp://purl.org/coar/resource_type/c_2df8fbb1
dc.typehttps://purl.org/redcol/resource_type/ART
dc.typeArtículo de investigación


Este ítem pertenece a la siguiente institución