| dc.description | o comportamento, frente ao envelhecimento físico, do sistema diglicidil éter do bisfenol-A (DGEBA) curado com diaminodifenilmetano (DOM) foi estudado em função da estrutura química, induzida pela cura, e do tempo de envelhecimento. Sistemas estequiométricos foram submetidos a Calorimetria Diferencial de Varredura (DSC) e Análise Térmica Dinâmico-Mecânica (DMTA). A cura isotérmica da resina epóxi foi realizada em uma etapa a 115°C e 135°C, por 20, 30, 45, 60 e 90 mino As amostras foram envelhecidas a 100°C por períodos de 4 até 72h. A extensão do envelhecimento físico foi associado com a área do pico endotérmico que aparece na região da transição vítrea, de acordo com os termogramas de DSC. Foi observado que a entalpia de relaxação aumenta gradualmente com o tempo de envelhecimento. Por DMT A, observou-se variações na magnitude do fator de perda (tan õ), no pico máximo, em função do grau de cura e do tempo de envelhecimento. O módulo dinâmico de armazenamento a 100°C (E'1CX)) deslocou-se para valores maiores assim como a Tg, medida através do pico a da curva log E", com o aumento do tempo de envelhecimento. A velocidade de envelhecimento e as energias de ativação da transição α foram obtidas a partir de parâmetros dinâmico-mecânicos e após associados com as diferentes histórias de cura e envelhecimento do material. De modo geral, a velocidade de envelhecimento (Ra) decresce com o aumento do grau de reticulação para sistemas curados a 115°C e passa por um mínimo para as amostras curadas a 135°C. As energias de ativação mostram uma tendência crescente com o tempo de envelhecimento. Concluiu-se que a técnica de DMTA é muito sensível às mudanças estruturais devido à cura e ao envelhecimento físico realizados nos sistemas investigados. Os resultados dinâmico-mecânicos obtidos para as misturas curadas segundo diferentes histórias térmicas salientam a importância da seleção adequada das condições de cura para que se possam obter as melhores propriedades destes materiais. | |
| dc.description | Physical aging behavior of diglycidyl ether of bisphenol-A (DGEBA) cured with diaminodiphenylmethane (DDM) have been investigated as a function of chemical structure, induced by cure, and aging time. Stoichiometric systems have been submitted to Differencial Scanning Calorimetry (DSC) and Dynamic Mechanical Thermal Analysis (DMTA) measurements. The isothermal curing of the epoxy resin was carried out in one step at 115°C and at 135°C for 20, 30, 45, 60 and 90 mino Samples were aged at 100°C for periods of time from 4 to a maximum of 72 h. The extent of physical aging has been measured by the area of the endothermic peak which appears within the glass transition region according to DSC thermograms. The enthalpy relaxation was found to increase gradually with aging time. Variations on magnitude of the loss factor (tan õ), on the maximum peak, have been observed as a function of degree of cure and aging time. The dynamic storage modulus at 100°C ( E' 100) changed with increasing physical aging to higher values as well as the glass transition temperature (Tg) as measured by the a peak on log E" curves. Aging rates and α transition activation energies were obtained through DMT A parameters analysis and then associated with different curing and aging histories of the material. Generally, the aging rate (Ra) decreases with increasing crosslinking degree for the systems cured at 115°C and passes through a minimum for those cured at 135°C. The activation energies demonstrate a tendecy to increase with aging time. It was concluded that the DMTA technique is very sensitive to structural changes in the investigated epoxy systems due to curing and physical aging . The DMTA results obtained from mixtures cured with different thermal histories underline the importance of adequate selection of curing conditions in order to obtain the optimum properties for these materiais. | |
| dc.format | application/pdf | |
| dc.language | por | |
| dc.rights | Open Access | |
| dc.subject | Análise térmica | |
| dc.subject | Resina epoxi : Reticulacao | |
| dc.subject | Envelhecimento físico | |
| dc.subject | Calorimetria exploratória diferencial - DSC | |
| dc.subject | Temperatura de transicao vitrea | |
| dc.title | Estudo do envelhecimento físico de sistemas epoxidílicos estequiométricos DGEBA/DDM através de análise térmica | |
| dc.type | Dissertação | |