| dc.contributor | Durand Orellana, Rocio del Pilar | |
| dc.creator | Requejo Amaya, Luis Alejandro | |
| dc.creator | Requejo Amaya, Luis Alejandro | |
| dc.date | 2021-03-24T22:29:43Z | |
| dc.date | 2021-03-24T22:29:43Z | |
| dc.date | 2021-03-24T22:29:43Z | |
| dc.date | 2021-03-24T22:29:43Z | |
| dc.date | 2021 | |
| dc.date.accessioned | 2023-08-08T02:07:10Z | |
| dc.date.available | 2023-08-08T02:07:10Z | |
| dc.identifier | https://hdl.handle.net/20.500.12759/7313 | |
| dc.identifier.uri | https://repositorioslatinoamericanos.uchile.cl/handle/2250/7988563 | |
| dc.description | La presente investigación tuvo como objetivo evaluar los efectos en las propiedades físicas -
mecánicas de concretos 210 y 280 kg/cm2 al sustituir material cementicio por costra, la cual es
un residuo que se produce en el interior del horno durante el proceso de la elaboración del
clínker. Por lo cual, se comparó a un concreto patrón versus concretos experimentales.
La investigación se centró en especímenes cilíndricos y prismáticos de concreto, los cuales
fueron elaborados con Cemento Pacasmayo tipo I, agregados fino y grueso que fueron
muestreados de la pila de agregados de Dino S.R.L y costra que fue recolectada de la zona
de desmonte de la empresa Cementos Pacasmayo S.A.A, la misma que fue molida hasta llegar
a una determinada finura. Asimismo, se evalúo la actividad puzolánica de la costra según las
normas ASTM C311 y ASTM C989.
Se realizaron 8 diferentes tipos de diseños (4 para concretos 210 kg/cm2 y 4 para concretos
280 kg/cm2
) según el método Módulo de fineza combinación de los agregados, los mismos
que fueron dosificados en proporciones de 0%, 20%, 35% y 50% de sustitución. Las muestras
estuvieron conformadas por 96 especímenes cilíndricos de 4 x 8” a los que se les evaluó su
resistencia a la compresión a 1, 3, 7 y 28 días; 24 especímenes cilíndricos de 6 x 12” a los que
se les evaluó su permeabilidad al aire y resistividad eléctrica; y 16 especímenes prismáticos
(vigas) de 22 x 6 x 6” a los que se les evaluó su resistencia a la flexión a los 28 días. Así mismo
a cada diseño se les evalúo su temperatura, consistencia (asentamiento) y peso unitario, de
los cuales se obtuvieron concretos del tipo normal con asentamientos entre 5” - 6”
clasificándolos de esta manera como mezclas fluidas.
Como conclusión, se obtuvo que el porcentaje de sustitución óptimo de costra por cemento es
al 20%, ya que es ahí donde se halla un balance entre costo-desempeño, teniendo
incrementos respecto a resistencia a la compresión, manteniendo la resistencia a la flexión,
permeabilidad y resistividad eléctrica. Además, es un 10% más económico que los diseños
patrón y contribuye de manera positiva al cuidado del medio ambiente como consecuencia de
la reducción de emisión de C02 al ambiente al utilizar menor cantidad de cemento. | |
| dc.description | The objective of this research was to evaluate the effects on the physical-mechanical properties
of 210 and 280 kg / cm2 concrete when substituting cementitious material for crust, which is a
residue that is produced inside the kiln during the process of making the clinker. Therefore, it
was compared to a concrete pattern versus concrete experimental.
The research focused on cylindrical and prismatic concrete specimens, which were made with
Cemento Pacasmayo type I, fine and coarse aggregates that were sampled from the pile of
aggregates of Dino S.R.L and crust that was collected from the company's clearing area.
Cementos Pacasmayo S.A.A, the same one that was ground to a certain fineness. Likewise,
the pozzolanic activity of the crust was evaluated according to the ASTM C311 and ASTM
C989 standards.
Eight different types of designs were made (4 for concretes 210 kg/cm2 and 4 for concretes
280 kg/cm2
) according to the method Modulus of fineness combination of the aggregates, which
were dosed in proportions of 0%, 20%, 35 % and 50% replacement. The samples consisted of
96 4 x 8” cylindrical specimens that were evaluated for their compressive strength at 1, 3, 7
and 28 days; 24 cylindrical specimens of 6 x 12” which were evaluated for their air permeability
and electrical resistivity; and 16 prismatic specimens (beams) of 22 x 6 x 6" which were
evaluated for their flexural strength at 28 days. Likewise, each design was evaluated for its
temperature, consistency (settlement) and unit weight, from which normal-type concretes with
settlements between 5 "- 6" were obtained, thus classifying them as fluid mixtures.
As a conclusion, it was obtained that the optimum percentage of substitution of crust for cement
is 20%, since it is there where there is a balance between cost-performance, having increases
with respect to compressive strength, maintaining flexural strength, permeability and electrical
resistivity. In addition, it is 10% cheaper than standard designs and contributes positively to
caring for the environment as a consequence of the reduction of C02 emissions to the
environment by using less cement. | |
| dc.description | Tesis | |
| dc.format | application/pdf | |
| dc.language | spa | |
| dc.publisher | Universidad Privada Antenor Orrego - UPAO | |
| dc.publisher | PE | |
| dc.relation | T_ING.CIVIL_1933 | |
| dc.rights | info:eu-repo/semantics/openAccess | |
| dc.source | Universidad Privada Antenor Orrego | |
| dc.source | Repositorio Institucional - UPAO | |
| dc.subject | Costra | |
| dc.subject | Concreto | |
| dc.subject | Material cementicio | |
| dc.subject | Sustitución | |
| dc.subject | Propiedades físicas | |
| dc.subject | http://purl.org/pe-repo/ocde/ford#2.01.01 | |
| dc.title | Efecto en las propiedades físicas-mecánicas del concreto con resistencias 210 y 280 kg/cm² al sustituir material cementicio por costra producto de la elaboración del Clínker | |
| dc.type | info:eu-repo/semantics/bachelorThesis | |