Grãos ultrafinos por laminação a morno e recozimento intercrítico

Abstract

Grain refinement of low carbon steel via the warm deformation of martensite during torsion testing was investigated. At the beginning of straining, laths with high dislocation density were observed. After large deformations, a ferrite matrix with grain size close to 1μm and dispersed cementite particles were attained.