dc.date.issued2002-12-02
dc.identifierMaterials Science Forum, v. 403, p. 39-44.
dc.identifier0255-5476
dc.identifierhttp://hdl.handle.net/11449/67145
dc.identifier10.4028/www.scientific.net/JMNM.14.39
dc.identifierWOS:000177650100006
dc.identifier2-s2.0-0036431938
dc.identifier9220348583560043
dc.identifier0000-0001-7040-1983
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/3916831
dc.description.abstractThe effect of bath composition and electroplating conditions on structure, morphology and composition of amorphous Fe-Cr-P-Ni-C deposits on Cu substrate was investigated. The deposition efficiency of Fe-Ni-P-C alloy increased significantly with the addition of formic acid, but decreased with the addition of Cr to the plating bath. The increase of charge density activates the inclusion of Cr in the deposit. However, above a specific value of charge density, which depends on deposition current density, the Cr content in the deposit decreases. SEM analysis showed that the increase of Ni, Cr or charge deposition promotes susceptibility to microcracking.
dc.languageeng
dc.relationMaterials Science Forum
dc.relation0,180
dc.rightsAcesso aberto
dc.sourceScopus
dc.subjectAlloys
dc.subjectAmorphous
dc.subjectElectrodeposition
dc.subjectCharge density
dc.subjectComposition
dc.subjectCurrent density
dc.subjectDeposits
dc.subjectElectroplating
dc.subjectIron alloys
dc.subjectMicrocracking
dc.subjectMorphology
dc.subjectScanning electron microscopy
dc.subjectAmorphous alloys
dc.titleElectrodeposition of amorphous Fe-Cr-P-Ni-C alloys. Morphological and structural characteristics