This paper presents the results of a study on the effect of expanded clay on the microstructure of the interfacial transition zone (ITZ) between Portland cement paste and aggregates. A scanning electron microscope (SEM) equipped with an energy dispersive X-ray analysis system (EDX) was used to determine the ITZ thickness. In plain concrete a marked ITZ around the aggregate particles (55   ?m) was observed, while in concretes with expanded clay, the ITZ was less pronounced (30 ?m). It was also verified that the ITZ of concrete with expanded clay had lower levels of porosity and calcium hydroxide than that observed in plain concrete.Este trabalho apresenta os resultados de uma pesquisa sobre o efeito do agregado leve brasileiro (argila expandida) na zona de transição pasta/agregado em concretos leves estruturais. Utilizou-se um microscópio eletrônico de varredura (MEV) associado a um sistema de análise quantitativa (espectrografia de raios X por dispersão de energias – EDS) para a avaliação da espessura da zona de transição. No concreto de referência, com brita basáltica, a zona de transição apresentou espessura de 55 mm, enquanto nos concretos com argila expandida observou-se a redução desse valor para 30 mm. Verificou-se, ainda, que a zona de transição dos concretos com argila expandida apresentou menores teores de poros e de hidróxido de cálcio do que o observado nos concretos com brita basáltica.