| dc.contributor | Rocha, Janaíde Cavalcante | |
| dc.contributor | Universidade Federal de Santa Catarina | |
| dc.creator | Jochem, Lidiane Fernanda | |
| dc.date | 2018-05-24T04:03:41Z | |
| dc.date | 2018-05-24T04:03:41Z | |
| dc.date | 2017 | |
| dc.date.accessioned | 2018-10-31T20:34:39Z | |
| dc.date.available | 2018-10-31T20:34:39Z | |
| dc.identifier | 352047 | |
| dc.identifier | https://repositorio.ufsc.br/handle/123456789/186519 | |
| dc.identifier.uri | http://repositorioslatinoamericanos.uchile.cl/handle/2250/1786937 | |
| dc.description | Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2017 | |
| dc.description | O crescente interesse no desenvolvimento sustentável, com o número de instalações de britagem dos resíduos de construção civil no país, produ-zindo agregados reciclados, faz a utilização desses agregados uma prio-ridade. Um modo de aumentar o consumo desse material é como agente de cura interna (CI), que tem como objetivo fornecer água adicional para a hidratação do cimento, sendo essa água fornecida por reservatórios internos (agregados porosos e absorventes). Assim, esse trabalho buscou verificar o potencial de ação como agente de cura interna e sorvente químico do agregado reciclado, para isso foram produzidas argamassas com substituição parcial (25 %) do agregado natural por agregado leve (ALV) ou agregado reciclado (RCC). As argamassas foram preparadas com os agregados (ALV e RCC) nas condições secas e saturadas previamente por 24 horas e o consumo de água dos agregados descontado da relação água/cimento inicial. Como também, em um primeiro momento foram preparadas, argamassas com cromo (Cr6+), chumbo (Pb4+) e zinco (Zn2+), para verificar o potencial de sorvente químico do agregado e de retenção das argamassas fabricadas com a realização da CI. Em um segundo momento foram preparadas argamassas com resíduo de galvanoplastia no estado líquido. Avaliou-se, em seguida, o desempenho mecânico e caracterizou-se a microestrutura em diferentes tempos de hidratação do cimento (de 1 a 90 dias). Foram utilizadas técnicas de RMN, DRX, MEV e avaliadas a liberação dos metais pelo ensaio de lixiviação e solubilização. O potencial de liberação de água dos agregados em elevadas umidades relativas foi verificado com o auxílio do ensaio de isotermas de dessorção nas frações (0,6 a 2,4 mm) do RCC e ALV e constatado que os agregados podem ser utilizados como agentes de CI. Assim como, concluiu-se que o RCC pode ser utilizado como sorvente químico, absorvendo/ adsorvendo, praticamente, 100 % do chumbo e do zinco e 15 % do cromo devido ao seu pH elevado. Os agregados apresentam diferenças no período de liberação da água dos poros, dependendo do seu estado inicial (seco ou saturado). Quando o agregado foi utilizado saturado auxiliou nas idades iniciais e quando foi utilizado seco previamente, auxiliou na melhora das propriedades físicas e mecânicas no período tardio. Por fim, constatou-se que o RCC pode ser utilizado como agente de CI e como um sorvente químico eficaz, aumentando o seu potencial de utilização além de não trazer prejuízos para o produto final. | |
| dc.description | Abstract: The growing interest in sustainable development, with the number of crushing facilities for construction and demolition waste in the country, producing recycled aggregates, makes the use of recycled aggregates from construction waste a priority. One way to increase the consumption of this material is as an internal curing agent, which aims to provide additional water for the hydration of the cement, being this water provided by internal reservoirs (porous and absorbent aggregates) which are, usually, previously saturated to preparation of the cementitious material. Thus, this work sought to verify the potential of recycled aggregate as internal curing agent and chemical sorbent. For this, mortars were produced with partial replacement (25%) of the natural aggregate by lightweight aggregate (ALV) or recycled aggregate (RCC). The mortars were prepared with the aggregates (ALV and RCC) dried and previously saturated for 24 hours and the water consumption of the aggregates discounted from the initial a/c ratio. Mortars with chromium (Cr6+), lead (Pb4+) and zinc (Zn2+) were also prepared to verify the chemical sorbent potential of the aggregate and the retention of mortars made with internal curing. The mechanical performance was evaluated and the microstructure was characterized in different times of cement hydration (1, 3, 7, 28 and 90 days). NMR, XRD, SEM and the release of the metals by the leaching test. The water release potential of the aggregates at high relative humidity was verified using the desorption isotherms test in the fractions (0.6 to 2.4 mm) of the lightweight and recycled aggregate and was found that the aggregates can be used as agents of internal curing. As well, was concluded that RCC could be used as a chemical sorbent, absorbent/adsorbent, practically 100 % of lead and zinc and 15 % of chromium due to its high pH. It was noticed that the aggregates present differences in the period of water release from the pores, depending on the initial state (dry or saturated) of the aggregate. When used saturated, the aggregate helped in the initial ages and when the aggregate was used dry previously helped in the improvement of properties in the late period. Finally, it was noticed that the recycled aggregate can be used as an internal curing agent and as an effective chemical sorbent, increasing it s potential for use and not to damage the final product. | |
| dc.format | xxviii, 299 p.| ils., grafs., tabs. | |
| dc.format | application/pdf | |
| dc.language | por | |
| dc.subject | Engenharia civil | |
| dc.subject | Cimento portland | |
| dc.subject | Solidificação | |
| dc.subject | Argamassa | |
| dc.subject | Resistência de materiais | |
| dc.title | Efeito do agregado reciclado dos resíduos de construção e demolição na retenção dos metais pesados em processos de solidificação e estabilização | |
| dc.type | Tese (Doutorado) | |