Thermal expansion coefficient, mechanical and structural properties of hydrogenated carbon nitrides
Registro en:
Diamond And Related Materials. Elsevier Science Sa, v. 25, n. 124, n. 127, 2012.
0925-9635
WOS:000304736900024
10.1016/j.diamond.2012.02.021
Autor
Champi, A
Marques, FC
Institución
Resumen
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) Amorphous hydrogenated carbon nitride films (a-C:H:N) deposited by plasma enhanced chemical vapor deposition of methane (CH4) and nitrogen (N-2), under low (-200 V) and high (-800 V) bias voltage are investigated. The nitrogen content was obtained from X-ray photoelectron spectroscopy and nuclear reaction analysis. Raman measurements were performed at 514 nm (visible) and 244 nm (UV) wavelengths. Mechanical properties (Young's modulus and hardness) and thermal expansion coefficient (TEC) were studied using the bending beam method. Raman spectroscopy shows that the incorporation of nitrogen in a-C:H reduces the disorder in the film, independent of the initial structure of the a-C:H films (tetrahedral-, diamond-, or graphitic-like). The TEC is related to the Raman parameters associated with the degree of sp(2) ordering (aromatic rings) in the film structure, increasing with the nitrogen incorporation. (C) 2012 Elsevier B.V. All rights reserved. 25 124 127 FAEP Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)