Evaluation of microcrack formation of ABNT M2 high speed steel in the EDM process, with addition of silicon carbide powder

dc.creatorRodrigues, JRP
dc.creatorCruz, C
dc.creatorFranco, SD
dc.creatorRodrigues, JRP
dc.creatorde Assuncao, W
dc.date2008
dc.date2014-07-30T17:28:04Z
dc.date2015-11-26T17:40:22Z
dc.date2014-07-30T17:28:04Z
dc.date2015-11-26T17:40:22Z
dc.date.accessioned2018-03-29T00:22:03Z
dc.date.available2018-03-29T00:22:03Z
dc.identifierActa Scientiarum-technology. Univ Estadual Maringa, Pro-reitoria Pesquisa Pos-graduacao, v. 30, n. 2, n. 173, n. 179, 2008.
dc.identifier1806-2563
dc.identifierWOS:000261859900007
dc.identifier10.4025/actascitechnol.v30i2.543
dc.identifierhttp://www.repositorio.unicamp.br/jspui/handle/REPOSIP/65858
dc.identifierhttp://repositorio.unicamp.br/jspui/handle/REPOSIP/65858
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/1286708
dc.descriptionEvaluation of microcrack formation of ABNT M2 high speed steel in the EDM process, with addition of silicon carbide powder. It is known that Electrical Discharge Machining (EDM) is a thermal process in which extremely high temperatures (in excess of 1200 degrees C) can occur in the machining area. Consequently, it is easy to understand that during each electric discharge, high temperatures are generated, causing local fusion or even evaporation of the machined material. In each discharge, a crater is formed in the material and a small crater is formed in the electrode. Of every melted material produced in each discharge, only 15% or less is removed using dielectric fluid. The remaining melted material solidifies, forming a wrinkled surface. The characteristics of the obtained surface - overlap of craters, globules of sullage, chimneys, bubbles (formed when the gases arrested are liberated through the resolidified material) - are revealed through an analysis using a scanning electron microscope. The proposed work has as its objective to study the effect of the addition of SiC powder into several dielectric fluids, on microcrack formation of high-speed steel (ABNT M2), during electrical discharge machining. The results show that the samples machined with the addition of SiC powders presented significant reduction in the number of microcracks in the machined surface, when compared with those machined with conventional EDM.
dc.description30
dc.description2
dc.description173
dc.description179
dc.languagept
dc.publisherUniv Estadual Maringa, Pro-reitoria Pesquisa Pos-graduacao
dc.publisherMaringa
dc.publisherBrasil
dc.relationActa Scientiarum-technology
dc.relationActa Sci.-Technol.
dc.rightsaberto
dc.sourceWeb of Science
dc.subjectelectrical discharge machining
dc.subjectdielectric fluids
dc.subjectpowder of SiC
dc.subjectcraters
dc.subjectmicrocrack formation
dc.titleEvaluation of microcrack formation of ABNT M2 high speed steel in the EDM process, with addition of silicon carbide powder