dc.creatorRoeder, J
dc.creatorOliveira, RVB
dc.creatorGoncalves, MC
dc.creatorSoldi, V
dc.creatorPires, ATN
dc.date2002
dc.dateOCT
dc.date2014-11-19T02:25:59Z
dc.date2015-11-26T17:00:58Z
dc.date2014-11-19T02:25:59Z
dc.date2015-11-26T17:00:58Z
dc.date.accessioned2018-03-28T23:48:46Z
dc.date.available2018-03-28T23:48:46Z
dc.identifierPolymer Testing. Elsevier Sci Ltd, v. 21, n. 7, n. 815, n. 821, 2002.
dc.identifier0142-9418
dc.identifierWOS:000176505100013
dc.identifier10.1016/S0142-9418(02)00016-8
dc.identifierhttp://www.repositorio.unicamp.br/jspui/handle/REPOSIP/70769
dc.identifierhttp://www.repositorio.unicamp.br/handle/REPOSIP/70769
dc.identifierhttp://repositorio.unicamp.br/jspui/handle/REPOSIP/70769
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/1278613
dc.descriptionThe influence of maleic anhydride grafted polypropylene (PP-g-MA) at the interface of immiscible, polypropylene (PP)/polyamide-6 (PA6) blends was studied by infrared spectroscopy, differential scanning calorimetry and transmission and scanning electron microscopy. The formation of a new copolymer at the interface between the domains and the matrix was investigated. The characterization of the interfacial copolymer was accomplished by carbonyl vibration of the imide group at 1674 cm(-1). The reduction of water absorption and the thermoanalysis experiments corroborated the imide linkage between the amino end groups of PA6 and the carboxylic groups of PP-g-MA. The modification of the PA6 particle size and the formation of the interfacial layer were characterized by microscopy and related to the reaction of the interfacial components. (C) 2002 Published by Elsevier Science Ltd.
dc.description21
dc.description7
dc.description815
dc.description821
dc.languageen
dc.publisherElsevier Sci Ltd
dc.publisherOxford
dc.publisherInglaterra
dc.relationPolymer Testing
dc.relationPolym. Test
dc.rightsfechado
dc.rightshttp://www.elsevier.com/about/open-access/open-access-policies/article-posting-policy
dc.sourceWeb of Science
dc.subjectblend
dc.subjectpolypropylene
dc.subjectpolyamide-6
dc.subjectinterface domains
dc.subjectmaleic anhydride grafted polypropylene
dc.subjectEthylene-propylene Rubber
dc.subjectPolypropylene/nylon-6 Blends
dc.subjectMorphology
dc.subjectNylon-6
dc.subjectCopolymer
dc.subjectEpdm
dc.subjectMa
dc.titlePolypropylene/polyamide-6 blends: influence of compatibilizing agent on interface domains