Synchrotron X-ray Multiple Diffraction In The Study Of Fe+ Ion Implantation In Si(0 0 1)
Registro en:
Journal Of Physics D: Applied Physics. , v. 42, n. 19, p. - , 2009.
223727
10.1088/0022-3727/42/19/195401
2-s2.0-70350624542
Autor
Dos Santos A.O.
Lang R.
De Menezes A.S.
Meneses E.A.
Amaral L.
Reboh S.
Cardoso L.P.
Institución
Resumen
In this work, x-ray multiple diffraction has been used as a three-dimensional high-resolution probe to study the Fe+ ion implantation process in Si(0 0 1). The semiconducting β-FeSi2 crystallographic phase has been synthesized by Fe ion co-implantation in Si(0 0 1) followed by ion-beam-induced epitaxial crystallization (IBIEC) and thermal treatment. This phase was clearly detected by the conventional techniques, micro-Raman scattering spectroscopy, transmission electron microscopy (TEM) and grazing incidence x-ray diffraction. Synchrotron radiation rocking curves (ω-scans) and mapping of the Bragg surface diffraction (BSD) of the Si matrix, as-implanted, after the IBIEC process and thermally treated, have enabled the detection of co-implanted regions formation that present distinct lattices in comparison with the matrix one clearly observed by TEM. Also, the compressive strain of both regions in depth by rocking curve and in-plane has been determined by using BSD, which is one order of magnitude smaller. © 2009 IOP Publishing Ltd. 42 19
Bost, M.C., Mahan, J.E., (1985) J. Appl. Phys., 58 (7), p. 2696 Leong, D.N., Harry, M.A., Reeson, K.J., Homewood, K.P., (1996) Appl. Phys. Lett., 68 (12), p. 1649 Lefki, K., Muret, P., (1993) J. Appl. Phys., 74 (2), p. 1138 Leong, D.N., Harry, M.A., Reeson, K.J., Homewood, K.P., (1997) Nature, 387 (6634), p. 686 Christensen, N.E., (1990) Phys. Rev., 42 (11), p. 7148 Clark, S.J., Al-Allak, H.M., Brand, S., Abram, R.A., (1998) Phys. Rev., 58 (16), p. 10389 Miglio, L., Meregalli, V., Jepsen, O., (1999) Appl. Phys. Lett., 75 (3), p. 385 Avanci, L.H., Cardoso, L.P., Girdwood, S.E., Pugh, D., Sherwood, J.N., Roberts, K.J., (1998) Phys. Rev. Lett., 81 (24), p. 5426 Avanci, L.H., Cardoso, L.P., Sasaki, J.M., Girdwood, S.E., Roberts, K.J., Pugh, D., Sherwood, J.N., (2000) Phys. Rev., 61 (10), p. 6507 Morelho, S.L., Cardoso, L.P., (1993) Solid State Commun., 88 (6), p. 465 Morelho, S.L., Avanci, L.H., Hayashi, M.A., Cardoso, L.P., Collins, S.P., (1998) Appl. Phys. Lett., 73 (15), p. 2194 Hayashi, M.A., Avanci, L.H., Cardoso, L.P., Bettini, J., De Carvalho, M.M.G., Morelho, S.L., Collins, S.P., (1999) J. Synchrotron Radiat., 6 (1), p. 29 Hayashi, M.A., Avanci, L.H., Cardoso, L.P., Sasaki, J.M., Kretly, L.C., Chang, S.L., (1997) Appl. Phys. Lett., 71 (18), p. 2614 Orloski, R.V., Pudenzi, M.A.A., Hayashi, M.A., Swart, J.W., Cardoso, L.P., (2005) J. Mol. Catal. A: Chem., 228 (1-2), p. 177 Chang, S.L., X-ray multiple-wave diffraction: Theory and applications (2004) Solid State Sciences, 143 Lai, X., Roberts, K.J., Bedzyk, M.J., Lyman, P.F., Cardoso, L.P., Sasaki, J.M., (2005) Chem. Mater., 17 (16), p. 4053 Sun, W.C., Chang, H.C., Wu, B.K., Chen, Y.R., Chu, C.H., Chang, S.L., Hong, M., Stetsko Yu, P., (2006) Appl. Phys. Lett., 89 (9), p. 091915 Morelho, S.L., Cardoso, L.P., (1996) J. Appl. Crystallogr., 29 (4), p. 446 Maltez, R.L., Amaral, L., Behar, M., Vantomme, A., Langouche, G., Lin, X.W., (1996) Phys. Rev., 54 (16), p. 11659 Priolo, F., Rimini, E., (1990) Mater. Sci. Rep., 5 (6), p. 319 Malegori, G., Miglio, L., (1993) Phys. Rev., 48 (13), p. 9223 Lefki, K., Muret, P., Bustarret, E., Boutarek, N., Madar, R., Chevrier, J., Derrien, J., Brunel, M., (1991) Solid State Commun., 80 (10), p. 791 Maeda, Y., Udono, H., Terai, Y., (2004) Thin Solid Films, 461 (1), p. 165 Dederichs, P.H., (1971) Phys. Rev., 4 (4), p. 1041