Structure And Properties Of Water Free Nd2o3 Doped Low Silica Calcium Aluminate Glasses
Registro en:
Journal Of Non-crystalline Solids. Elsevier Science Publishers B.v., Amsterdam, Netherlands, v. 247, n. , p. 196 - 202, 1999.
223093
10.1016/S0022-3093(99)00062-9
2-s2.0-0032660126
Autor
Sampaio J.A.
Catunda T.
Gandra F.C.G.
Gama S.
Bento A.C.
Miranda L.C.M.
Baesso M.L.
Institución
Resumen
In this work, Nd2O3 doped low silica calcium aluminate glasses have been melted under vacuum conditions. Measurements of thermal diffusivity, density, optical absorption coefficient, glass transformation temperature (Tg), crystallisation temperature (Tx), dilatometric softening temperature (Td) and Vickers microhardness have been carried out. The results provided information about the sample's structure and showed that for Nd2O3 concentration up to 5 wt% there was no devitrification of the samples. The decrease in hardness and thermal diffusivity was about 8%, while the density increased about 8% with the increasing concentration of Nd2O3. The thermomechanical properties combined with their quantum efficiency indicate that this material is a candidate for an active medium for solid-state lasers. 247
196 202 Florence, J.M., Glaze, F.W., Black, M.H., (1955) J. Res. NBS, 55 (4), p. 231 Hafner, H.C., Kreidl, N.J., Weidel, R.A., (1958) J. Am. Ceram. Soc., 41 (8), p. 315 Onoda G.Y., Jr., Brown, S.D., (1970) J. Am. Ceram. Soc., 53 (6), p. 311 Davy, J.R., (1978) Glass Technol., 19 (2), p. 33 Shelby, J.E., (1985) J. Am. Ceram. Soc., 68 (3), p. 155 Higby, P.L., Ginther, R.J., Aggarwal, I.D., Friebele, E.J., (1990) J. Non-Cryst. Solids, 126, p. 209 King, W.A., Shelby, J.E., (1996) Phys. Chem. Glasses, 37 (1), p. 1 Tanabe, S., Ohyagi, T., Hanada, T., Soga, N., (1993) J. Am. Ceram. Soc. Japan, 101, p. 78 Hirao, K., Todoroki, S., Soga, N., (1992) Bol. Soc. Espan. Ceram. Vid., 81 C, p. 121 Baesso, M.L., Bento, A.C., Andrade, A.A., Sampaio, J.A., Pecoraro, E., Nunes, L.A.O., Catunda, T., Gama, S., (1998) Phys. Rev. B, 57, p. 10545 Baesso, M.L., Bento, A.C., Andrade, A.A., Sampaio, J.A., Catunda, T., Gama, S., (1997) J. Non-Cryst. Solids, 219, p. 139 Chung, W.J., Yoo, J.R., Kim, Y.S., Heo, J., (1997) J. Am. Ceram. Soc., 80 (6), p. 1485 Uhlmann, E.V., Weinberg, M.C., Kreidl, N.J., (1994) J. Non-Cryst. Solids, 178, p. 15 Zou, X.L., Izumitani, T., (1993) Nippon Seram Kyo Gak, 101 (1), p. 99 Koechner, W., (1966) Solid State Laser Engenineering, 4th Ed., , Spring, Berlin Gan, F., (1994) Laser Materials, , World Scientific, Singapore Deutschbein, O., Faulstich, M., Jahn, W., Krolla, G., Neuroth, N., (1978) Appl. Opt., 17, p. 2228 Fernandes, J., Balda, R., Arriandiaga, M.A., (1994) Opt. Mater., 4, p. 91 Ebendorff-Heidepriem, H., Seeber, W., Ehrt, D., (1995) J. Non-Cryst. Solids, 183, p. 191 Kohli, J.T., Shelby, J.E., (1991) Phys. Chem. Glasses, 32, p. 67 Shelby, J.E., Kohli, J.T., (1990) J. Am. Ceram. Soc., 73, p. 39 Baesso, M.L., Shen, J., Snook, R.D., (1992) Chem. Phys. Lett., 195, p. 255 Baesso, M.L., Shen, J., Snook, R.D., (1994) J. Appl. Phys., 75, p. 3232 Oprea, C., Togan, D., Popescu, C., (1992) Thermochim. Acta, 194, p. 165 Lucas, L., Chanthanasinh, M., Poulain, M., Poulain, M., Brun, P., Weber, M.J., (1978) J. Non-Cryst. Solids, 27, p. 273 Chopra, S.K., Tanera, C.A., (1965) J. Appl. Chem., 15, p. 157 Mansanares, A.M., Baesso, M.L., Da Silva, E.C., Gandra, F.C.G., Vargas, H., Miranda, L.C.M., (1989) Phys. Rev. B, 40, p. 7912