Bioreabsorbable polymers are routinely used as temporary prostheses for fractured bones. Among the bioreabsorbable polymers the poly(L-co-D, L lactic acid), PLDLA, in the 70:30 rate has been studied to obtain plates and screws to recuperate traumas in the cranium and maxilla facial regions. In this monomers rate, an amorphous polymer is obtained, which allows adaptation of devices in the local for the implant during the surgery. A limiting factor to use this polymer is its high cost, due to the importation process. In this work PLDLA was synthesized by mass polymerization of the cyclical monomers L-lactic acid and D, L lactic acid, using Sn(Oct)2 as catalyst. A material with high molar mass (10(5) g/mol) was obtained and characterized by ¹H RMN, 13C RMN, GPC, FTIR and DSC.A aplicação de polímeros biorreabsorvíveis em próteses temporárias é constante nos procedimentos médicos relacionados a fraturas ósseas. Dentre os polímeros bioreabsorvíveis, o poli(L-co-D, L ácido láctico), PLDLA, na relação 70:30, tem sido estudado visando à obtenção de placas e parafusos para a recuperação de traumas nas regiões buco e crâniomaxilofacial. Nessa relação de monômeros obtém-se um polímero amorfo, o que permite uma adaptação do dispositivo ao local do implante durante a cirurgia. Um fator limitante para o uso desse polímero é seu alto custo em função da importação. Neste trabalho o PLDLA foi sintetizado através da polimerização em massa dos monômeros cíclicos do L-ácido láctico e do D, L ácido láctico, utilizando como catalisador o Sn(Oct)2. Obteve-se material de alta massa molar (Mw = 10(5) g/mol), o qual foi caracterizado por ¹H RMN, 13C RMN, GPC, FTIR e DSC.123129