Evaluation of strip rolling directly from the semi-solid state
(Trans Tech Publications Ltd, 2014)
Evaluation of strip rolling directly from the semi-solid state
(Trans Tech Publications Ltd, 2006-01-01)
defect metal alloy strip when thixorolling directly from the semi-solid state. To facilitate the study lead/tin alloys were chosen for their relatively low operating temperature. The objective is to extrapolate these ...
Evaluation of strip rolling directly from the semi-solid state
(Trans Tech Publications Ltd, 2006-01-01)
defect metal alloy strip when thixorolling directly from the semi-solid state. To facilitate the study lead/tin alloys were chosen for their relatively low operating temperature. The objective is to extrapolate these ...
Evaluation of strip rolling directly from the semi-solid state
(2006-01-01)
The aim of this work is to study the solidification conditions necessary to produce good quality/low defect metal alloy strip when thixorolling directly from the semi-solid state. To facilitate the study lead/tin alloys ...
Fabricação e caracterização metalográfica e mecânica de tiras de ligas metálicas fundidas e tixolaminadas no estado semi-sólido de diferentes intervalos de solidificação
(Universidade Estadual Paulista (UNESP), 2014)
Fabricação e caracterização metalográfica e mecânica de tiras de ligas metálicas fundidas e tixolaminadas no estado semi-sólido de diferentes intervalos de solidificação
(Universidade Estadual Paulista (Unesp), 2008-09-03)
É apresentado um estudo experimental da laminação de tiras fundidas a partir do material semi-sólido obtido na calha de resfriamento que alimenta continuamente um laminador duo. Os cilindros do laminador estão posicionados ...
Fabricação e caracterização metalográfica e mecânica de tiras de ligas metálicas fundidas e tixolaminadas no estado semi-sólido de diferentes intervalos de solidificação
(Universidade Estadual Paulista (Unesp), 2008-09-03)
É apresentado um estudo experimental da laminação de tiras fundidas a partir do material semi-sólido obtido na calha de resfriamento que alimenta continuamente um laminador duo. Os cilindros do laminador estão posicionados ...
A Comparison of Deep Drawing and Ironing of Metal Alloy Strip Produced conventionally and Non-conventionally via Semi Solid Material Processing
(Trans Tech Publications Ltd, 2008-01-01)
A semi solid thin strip continuous casting process was used to obtain 50%wt Pb/50%wtSn strip by single and twin roll processing at speed of 15 m/min. A 50%wt Pb/50%wtSn plate ingot was also cast for rolling conventionally ...
A Comparison of Deep Drawing and Ironing of Metal Alloy Strip Produced conventionally and Non-conventionally via Semi Solid Material Processing
(Trans Tech Publications Ltd, 2008-01-01)
A semi solid thin strip continuous casting process was used to obtain 50%wt Pb/50%wtSn strip by single and twin roll processing at speed of 15 m/min. A 50%wt Pb/50%wtSn plate ingot was also cast for rolling conventionally ...
A comparison of deep drawing and ironing of metal alloy strip produced conventionally and non-conventionally via semi solid material processing
(2008-01-01)
A semi solid thin strip continuous casting process was used to obtain 50%wt Pb/50%wtSn strip by single and twin roll processing at speed of 15 m/min. A 50%wt Pb/50%wtSn plate ingot was also cast for rolling conventionally ...