Extended X-ray absorption fine spectroscopy (EXAFS) and Raman scattering studies of InF3-BaF2 and InF3-SrF2 binary glasses are reported. For all compositions, the local structure of the glasses is built with InF6 units. ...

Extended X-ray absorption fine spectroscopy (EXAFS) and Raman scattering studies of InF3-BaF2 and InF3-SrF2 binary glasses are reported. For all compositions, the local structure of the glasses is built with InF6 units. ...

This paper describes the stabilizing effect of MgF2 on the binary system InF3-BaF2. A complete investigation of the In-Ba-Mg system led to samples up to 5 mm in thickness. Further optimization of this system was achieved ...

This paper describes the stabilizing effect of MgF2 on the binary system InF3-BaF2. A complete investigation of the In-Ba-Mg system led to samples up to 5 mm in thickness. Further optimization of this system was achieved ...

Very reactive, monodisperse (4.0 ± 0.5 nm) spherical indium(0) nanoparticles have been generated in situ, in a simple, mild and efficient way, by fast reduction of commercially available indium(iii) chloride with lithium ...

Results on thermal and optical characterization of new lanthanide containing fluoroindate glasses in the system InF3-BaF2-In(PO3)3 are presented. Good optical quality and very stable glasses presenting up to 5 mm in thickness ...

Results on thermal and optical characterization of new lanthanide containing fluoroindate glasses in the system InF3-BaF2-In(PO3)3 are presented. Good optical quality and very stable glasses presenting up to 5 mm in thickness ...