Effects of several TIG weld repairs on the axial fatigue strength of AISI 4130 aeronautical steel-welded joints
(Wiley-Blackwell, 2012-03-01)
Welded joints of airframes critical to the flight-safety are commonly repair welded during its operational live. In this study, the effect of up to three weld repairs by gas tungsten arc welding (GTAW) on the axial fatigue ...
Effects of several TIG weld repairs on the axial fatigue strength of AISI 4130 aeronautical steel-welded joints
(Wiley-Blackwell, 2012-03-01)
Welded joints of airframes critical to the flight-safety are commonly repair welded during its operational live. In this study, the effect of up to three weld repairs by gas tungsten arc welding (GTAW) on the axial fatigue ...
Fracture resistance of flash welded and laser welded butt joints in a microalloyed HSLA steel
(2017-01-01)
High-strength, low-alloy (HSLA) steels are widely used in the automotive and oil industries due to their good mechanical properties and weldability. The selection of the welding process depends on several factors, including ...
Fatigue Crack Growth Investigation on a Maintenance Welding Repair Applied on a High Responsibility Airframe
(Elsevier B.V., 2014-01-01)
Fatigue crack usually initiates at welded joints of structural elements. For a high-responsibility aeronautic component, called Motor-Cradle - critical to the flight safety -, successive weld repairs are carried out toward ...
Fatigue strength of tungsten inert gas-repaired weld joints in airplane critical structures
(Elsevier B.V. Sa, 2011-06-01)
In this work the effect of Gas Tungsten Arc Welding (GTAW) repairs on the axial fatigue strength of an AISI 4130 steel welded joint used in airframe critical to the flight-safety was investigated. Fatigue tests were performed ...
Fatigue strength of tungsten inert gas-repaired weld joints in airplane critical structures
(Elsevier B.V. Sa, 2011-06-01)
In this work the effect of Gas Tungsten Arc Welding (GTAW) repairs on the axial fatigue strength of an AISI 4130 steel welded joint used in airframe critical to the flight-safety was investigated. Fatigue tests were performed ...
Mechanical and microstructural characterization of laser-welded joints of 6013-T4 aluminum alloy
(Springer, 2015-01-01)
Laser beam welding may be used in the place of the traditional riveting process for the welding of the stringers to the skin in aircrafts. This work intends to investigate the mechanical behavior of laser-welded aluminum ...